UBE UBEPOL BR150B Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C)
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | UBE |
| Trade Name | UBEPOL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | UBE UBEPOL BR150B Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: UBEPOL BR is UBE's line of polybutadiene rubber products.Information provided by UBE.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 60 | 60 | ASTM D412 |
| Tensile Strength at Break | 16.2 MPa | 2350 psi | ASTM D412 |
| Elongation at Break | 450 % | 450 % | ASTM D412 |
| 100% Modulus | 0.00210 GPa | 0.305 ksi | ASTM D412 |
| 200% Modulus | 0.00530 GPa | 0.769 ksi | ASTM D412 |
| 300% Modulus | 0.00970 GPa | 1.41 ksi | ASTM D412 |
| Rebound | 54 % | 54 % | BS.903,PART22 |
| Tear Strength | 44.0 kN/m | 251 pli | ASTM D624 |
| Abrasion | 86 | 86 | Lombourn Abrasion Index (Iwamoto Seisakusyo, Japan); UBE Method |
| 183 | 183 | Pico Abrasion Index; ASTM D2228 | |
| Compression Set | 17 % | 17 % | Method B, 70°C, 72hrs; ASTM D395 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Cut Generation De Mattia Flexing Machine | Min 300,000 times | ASTM D430 |
| Cut Growth (2mm-->15mm) De Mattia Flexing Machine | 3100 times | ASTM D313 |
| Goodrich Flex, 0.175" Stroke, 55lb, 100°C, P.S. | 13% | ASTM D623 (36°C change in temperature) |
| Wet Skid Resistance on Safety-Walk | 19 | UBE Method (British Portable Skid Resistance Tester) |
Users viewing this material also viewed the following:
- Abatron 810319 A/B Filled Potting Compound (discontinued **)
- Ineos Nova 4214 Medium Impact Polystyrene (discontinued **)
- Taiwan Sheen Soon Sheenthane® D6010E Thermoplastic Polyurethane Elastomer
- SABIC Innovative Plastics NORYL NH8006 PPE+HIPS (Asia Pacific)
- Dow Corning SILASTIC® S-2 RTV SILICONE RUBBER BASE & CURING AGENT
- Fainplast Compounds HAX HF 018/9 Halogen Free PVC
- Azdel Plus R300B01N 30% Continuous Random Fiber Mat / PP Resin Matrix
- BASF Ultradur B 4300 G2 LS High Speed BK15045 10% Glass Filled PBT
Copyright © lookpolymers.com All Rights Reserved