Trelleborg Horda Cable E7310 Bonded Insulation Shielding And Conductor Screen

Category	Polymer , Thermoset
Manufacturer	Trelleborg Horda Cable Compounds
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Trelleborg Horda Cable E7310 Bonded Insulation Shielding And Conductor Screen.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

E7310 is a silane crosslinkable semiconductive compound for medium voltage cables. The material is designed as a conductor screen and bonded insulation shielding.E7310 meets the requirements as below, when optimal processing, extrusion and crosslinking procedure are used:BS 6622IEC 60502-2All information provided by Horda Cable Compounds

Physical Properties	Metric	English	Comments
Density	1.10 g/cc @Temperature 23.0 °C	0.0397 lb/in³ @Temperature 73.4 °F	ASTM D1928

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	85 - 90	85 - 90	ASTM D2240
Tensile Strength, Yield	19.0 MPa	2760 psi	after aging 1 week @ 135°C; ASTM D638
	20.0 MPa	2900 psi	ASTM D638
Elongation at Break	140 %	140 %	after aging 1 week @ 135°C; ASTM D638
	200 %	200 %	ASTM D638

Electrical Properties	Metric	English	Comments
Volume Resistivity	<= 100 ohm-cm @Temperature 23.0 °C	<= 100 ohm-cm @Temperature 73.4 °F	ASTM D257
	<= 1000 ohm-cm @Temperature 90.0 °C	<= 1000 ohm-cm @Temperature 194 °F	ASTM D257
	<= 1000 ohm-cm @Temperature 120 °C	<= 1000 ohm-cm @Temperature 248 °F	ASTM D257

Processing Properties	Metric	English	Comments
Drying Temperature	<= 60.0 °C	<= 140 °F	pellets below 300 PPM (Karl Fischer method)
Moisture Content	<= 0.050 %	<= 0.050 %	QAHC-10420 (Karl Fischer method)

Descriptive Properties	Value	Comments
Hot Set (%)	20/5	200°C, 20 N/cm²; IEC 540