Trelleborg Horda Cable E6352-A2 Bonded Semiconductive Shielding And Conductor Screen

Category	Polymer , Thermoset
Manufacturer	Trelleborg Horda Cable Compounds
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Trelleborg Horda Cable E6352-A2 Bonded Semiconductive Shielding And Conductor Screen.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

E6352-A2 is a crosslinkable semiconductive compound based on ethylene copolymer compound, designed for conductor screen and insulation shield applications in XLPE and EPDM insulated cables with bonded shield.E6342-A2Have good compatibility with copper and aluminum conductorsExcellent surface smoothnessGood scorch resistanceGood stability with high temperature curingAll information provided by Horda Cable Compounds

Physical Properties	Metric	English	Comments
Density	1.14 g/cc @Temperature 23.0 °C	0.0412 lb/in³ @Temperature 73.4 °F	ASTM D1928
Mooney Viscosity	25 @Temperature 121 °C	25 @Temperature 250 °F	ISO 289

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	85 - 90	85 - 90	ASTM D2240
Tensile Strength, Yield	14.25 MPa	2067 psi	after aging 1 week @ 135°C; ASTM D638
	15.0 MPa	2180 psi	ASTM D638
Elongation at Break	176 %	176 %	after aging 1 week @ 135°C; ASTM D638
	220 %	220 %	ASTM D638

Electrical Properties	Metric	English	Comments
Volume Resistivity	<= 100 ohm-cm @Temperature 23.0 °C	<= 100 ohm-cm @Temperature 73.4 °F	ASTM D257
	<= 1000 ohm-cm @Temperature 90.0 °C	<= 1000 ohm-cm @Temperature 194 °F	ASTM D257
	<= 1000 ohm-cm @Temperature 120 °C	<= 1000 ohm-cm @Temperature 248 °F	ASTM D257

Processing Properties	Metric	English	Comments
Middle Barrel Temperature	80.0 - 120 °C	176 - 248 °F
Head Temperature	115 - 125 °C	239 - 257 °F
Screw Cooling Temperature	50.0 - 70.0 °C	122 - 158 °F
Drying Temperature	<= 60.0 °C	<= 140 °F	Dehumidified hopper drying for up to five hours
Moisture Content	<= 0.060 %	<= 0.060 %	QAHC-10420 (Karl Fischer method)

Descriptive Properties	Value	Comments
Hot Set (%)	30-40	200°C, 20 N/cm²; IEC 540

Users viewing this material also viewed the following: