Tra-Con Tra-Bond 216L01 Clear Low Viscosity Epoxy Adhesive

Category Polymer , Adhesive , Thermoset , Epoxy
Manufacturer Tra-Con, Inc.
Trade Name Tra-Bond
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Tra-Con Tra-Bond 216L01 Clear Low Viscosity Epoxy Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TRA-BOND 216L01 is a clear, low viscosity epoxy adhesive system that contains no solvents, cures at room temperature, has excellent flowability and wetting characteristics, and adheres strongly to glass, ceramics, most metals and many plastics. It is particularly recommended for assembly and repair work of fiber optic and other high performance electronic and aerospace systems and components, and for structural laminating applications where an initial low viscosity and near transparent "color" are needed. Fully cured TRA-BOND 216L01 is a good electrical insulator, provides excellent resistance to weather, galvanic action, salt solutions and many other chemicals including mild acid and alkalis, petroleum solvents, lubricating oils, jet fuels and gasoline, and alcohol. Information provided by Tra-Con Inc.
Physical Properties Metric English Comments
Specific Gravity 1.16 g/cc
1.16 g/cc
Mixed
Viscosity 250 cP

@Temperature 25.0 °C
250 cP

@Temperature 77.0 °F
After mixing
Mechanical Properties Metric English Comments
Hardness, Shore D 88
88
Izod Impact, Notched 0.128 J/cm
0.240 ft-lb/in
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 130 °C
266 °F
Minimum Service Temperature, Air -60.0 °C
-76.0 °F
Glass Transition Temp, Tg 90.0 °C
194 °F
Ultimate Tg
Optical Properties Metric English Comments
Transmission, Visible 90 %
90 %
clear; thickness not quantified
Electrical Properties Metric English Comments
Volume Resistivity 6.00e+13 ohm-cm
6.00e+13 ohm-cm
1.00e+10 ohm-cm

@Temperature 100 °C
1.00e+10 ohm-cm

@Temperature 212 °F
Dielectric Constant 4.3

@Frequency 1000 Hz
4.3

@Frequency 1000 Hz
Dielectric Strength 16.1 kV/mm
410 kV/in
Dissipation Factor 0.020

@Frequency 1000 Hz
0.020

@Frequency 1000 Hz
Processing Properties Metric English Comments
Cure Time 60.0 - 240 min

@Temperature 65.0 °C
1.00 - 4.00 hour

@Temperature 149 °F
1440 min

@Temperature 25.0 °C
24.0 hour

@Temperature 77.0 °F
Pot Life 30 min
30 min
Descriptive Properties Value Comments
Color Clear, Transparent
Mix Ratio, parts by weight 100/11
Resin/Hardener