Toyobo VYLOPET® EMC605P PBT/PET Alloy, Anti-microbial
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polyethylene Terephthalate (PET) |
| Manufacturer | Toyobo |
| Trade Name | VYLOPET® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo VYLOPET® EMC605P PBT/PET Alloy, Anti-microbial.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Gas equipment partsFeatures: Good anti-microbialGood appearanceFlame resistantInformation provided by Toyobo.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 |
| Water Absorption | 0.060 % | 0.060 % | 24 hrs at 23°C; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.011 cm/cm @Thickness 3.00 mm |
0.011 in/in @Thickness 0.118 in |
MD |
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm @Thickness 3.00 mm |
0.012 in/in @Thickness 0.118 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 80 | 80 | ASTM D785 |
| Tensile Strength at Break | 48.0 MPa | 6960 psi | ASTM D638 |
| Elongation at Break | 3.2 % | 3.2 % | ASTM D638 |
| Flexural Strength | 80.0 MPa | 11600 psi | ASTM D790 |
| Flexural Modulus | 3.50 GPa | 508 ksi | ASTM D790 |
| Izod Impact, Notched | 0.400 J/cm | 0.749 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 µm/m-°C @Temperature 20.0 °C |
38.9 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Maximum Service Temperature, Air | 205 °C | 401 °F | Ball pressure temperature; ASTM UL746B |
| Deflection Temperature at 0.46 MPa (66 psi) | 185 °C | 365 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 24.0 kV/mm @Thickness 2.00 mm |
610 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Arc Resistance | 90 sec | 90 sec | Tungsten electrode; ASTM D495 |
| Comparative Tracking Index | 175 - 249 V | 175 - 249 V | IEC Pub1.112, class 3; IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 265 °C | 509 °F | Molding temperature |
| Mold Temperature | 80.0 °C | 176 °F | |
| Drying Temperature | 140 °C | 284 °F | |
| Dry Time | 3 hour | 3 hour |
Users viewing this material also viewed the following:
- MV Labs AG1500 Ag[O2C(CH2)3C6H11] Silver cyclohexanebutyrate
- Plenco 2424 Phenolic, Granular, Injection Molded (discontinued **)
- I. Stern GPPS-004 General Purpose Crystal Polystyrene
- Micropol Microcene MC122 Metallocene Based Polyethylene Rotational Molding Powder
- Kuraray SEPTON® A3 Hot Melt Adhesive
- Styrolution Terblend® N NM-19 XP Beige 38163 ABS+PA (Dry)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 0.0 PHR Zinc Stearate
- Ter Hell Plastic Terez® PC 9007 UV Polycarbonate
- Loctite® 5248 Silicone Adhesive
- SolVin 275SC Polyvinyl Chloride General Purpose - Plasticized
Copyright © lookpolymers.com All Rights Reserved