Toyobo TS101 PPS, Glass Fiber/Mineral Reinforced

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled
Manufacturer Toyobo
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Toyobo TS101 PPS, Glass Fiber/Mineral Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Key Feature: High dimensional stabilityHigh performance injection-molding resin created from crystalline polyphenylene sulfide, using a special formulation technology developed by Toyobo. Excellent physical, electrical, and thermal properties, corrosion resistant, and inherently flame retardant. PPS resins are used in the electrical, electronic, automotive, and industrial machinery industries.Information provided by Toyobo Co., Ltd
Physical Properties Metric English Comments
Density 2.09 g/cc
0.0755 lb/in³
ASTM D792
Water Absorption 0.020 %
0.020 %
24 hrs; ASTM D570
Linear Mold Shrinkage 0.0013 cm/cm
0.0013 in/in
Linear Mold Shrinkage, Transverse 0.0025 cm/cm
0.0025 in/in
Mechanical Properties Metric English Comments
Hardness, Rockwell R 121
121
ASTM D785
Tensile Strength, Ultimate 128 MPa
18600 psi
ASMT D638
Elongation at Break 0.70 %
0.70 %
ASTM D638
Modulus of Elasticity 26.5 GPa
3840 ksi
ASMT D638
Flexural Yield Strength 193 MPa
28000 psi
Flexural elongation is 1%; ASTM D790
Flexural Modulus 20.6 GPa
2990 ksi
ASMT D790
Izod Impact, Notched 1.00 J/cm
1.87 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 14.0 µm/m-°C

@Temperature 20.0 °C
7.78 µin/in-°F

@Temperature 68.0 °F
MD
CTE, linear, Transverse to Flow 32.0 µm/m-°C

@Temperature 20.0 °C
17.8 µin/in-°F

@Temperature 68.0 °F
Melting Point 282 °C
540 °F
Deflection Temperature at 1.8 MPa (264 psi) >= 260 °C
>= 500 °F
ASTM D648
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Dielectric Constant 5.3

@Frequency 1e+6 Hz
5.3

@Frequency 1e+6 Hz
ASTM D150
5.5

@Frequency 1000 Hz
5.5

@Frequency 1000 Hz
ASTM D150
Dielectric Strength 11.0 kV/mm
279 kV/in
ASTM D149
Dissipation Factor 0.0083

@Frequency 1e+6 Hz
0.0083

@Frequency 1e+6 Hz
ASTM D150
0.053

@Frequency 1000 Hz
0.053

@Frequency 1000 Hz
ASTM D150
Arc Resistance 182 sec
182 sec
ASTM D495
Comparative Tracking Index 275 V
275 V
IEC test