Toyobo PELPRENE™ P46D-01 Polyester TPE, High Viscous, High Durability
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester TPE , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | Toyobo |
| Trade Name | Pelprene™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo PELPRENE™ P46D-01 Polyester TPE, High Viscous, High Durability.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Polyester TPE, High Viscous, High DurabilityInformation provided by Toyobo.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.45 % | 0.45 % | 23°C, 65% RH |
| Linear Mold Shrinkage | 0.0070 cm/cm @Thickness 2.00 mm |
0.0070 in/in @Thickness 0.0787 in |
|
| Melt Index of Compound | 0.50 g/10 min @Temperature 230 °C |
0.50 g/10 min @Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 97 | 97 | JIS K6301 |
| Hardness, Shore D | 46 | 46 | ASTM D2240 |
| Tensile Strength at Break | 31.9 MPa | 4630 psi | ASTM D638 |
| Elongation at Break | 700 % | 700 % | ASTM D638 |
| 50% Modulus | 0.0109 GPa | 1.58 ksi | ASTM D638 |
| Flexural Modulus | 0.110 GPa | 16.0 ksi | ASTM D790 |
| Compressive Modulus | 0.00960 GPa | 1.39 ksi | 0.1; ASTM D695 |
| Resilience | 70 | 70 | JIS K6301 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Tear Strength | 165 kN/m | 941 pli | ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 10 | 10 | ASTM D1044 |
| Compression Set | 55 % | 55 % | JIS K6301 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 170 µm/m-°C @Temperature 20.0 °C |
94.4 µin/in-°F @Temperature 68.0 °F |
TMA |
| Melting Point | 203 °C | 397 °F | By DSC |
| Maximum Service Temperature, Air | 74.0 °C | 165 °F | Heat deflection temperature, load unknown; ASTM D648 |
| Vicat Softening Point | 153 °C | 307 °F | ASTM D1525 |
| Brittleness Temperature | <= -65.0 °C | <= -85.0 °F | JIS K6301 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.00e+13 ohm-cm | 4.00e+13 ohm-cm | ASTM D257 |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | JIS K2111 |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 2010 M Polypropylene
- Polymax® Maxelast® P3780H TPE, PP Overmold or Standalone use
- Lucas-Milhaupt BRAZE 716 (VTG) Grade 1 Silver Based Cadmium Free Filler Metal
- SABIC Innovative Plastics LNP STAT-LOY AF306 ABS (Asia Pacific)
- A. Schulman POLYBATCH™ Gardenia P80515PF Concentrate Based In Polypropylene
- DuPont Performance Polymers Delrin® II150E BK602 Acetal (POM)
- Aaron Industries AAROPRENE® ATPR 1000 70A Elastomeric Compound
- Aleris HOGAL 5558 Aluminum 5026 H14/H34
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 90A, Black Sulfur Cure
Copyright © lookpolymers.com All Rights Reserved