Toyobo GLAMIDE® T-663G50 Nylon-66

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled
Manufacturer	Toyobo
Trade Name	GLAMIDE®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Toyobo GLAMIDE® T-663G50 Nylon-66.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade T-663G50 is a GF reinforced Nylon-66. It contains 50% GF.50

Physical Properties	Metric	English	Comments
Specific Gravity	1.57 g/cc	1.57 g/cc	Absolute Drying; ASTM-D792
Filler Content	50 %	50 %
Water Absorption	0.40 %	0.40 %	Absolute Drying; ASTM-D570
Moisture Absorption at Equilibrium	1.2 %	1.2 %	Absolute Drying; ASTM-D570
Linear Mold Shrinkage	0.0020 - 0.0040 cm/cm @Thickness 1.00 mm	0.0020 - 0.0040 in/in @Thickness 0.0394 in	Absolute Drying
	0.0060 - 0.0080 cm/cm @Thickness 3.00 mm	0.0060 - 0.0080 in/in @Thickness 0.118 in	Absolute Drying
Melt Flow	4.0 g/10 min	4.0 g/10 min

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	121	121	Absolute Drying; ASTM-D785
Tensile Strength, Ultimate	115 MPa @Temperature 80.0 °C	16700 psi @Temperature 176 °F	Practical Use (Water Absorption 1.25%); ASTM-D638
	145 MPa @Temperature 80.0 °C	21000 psi @Temperature 176 °F	Absolute Drying; ASTM-D638
	160 MPa @Temperature 23.0 °C	23200 psi @Temperature 73.4 °F	Practical Use (Water Absorption 1.25%); ASTM-D638
	215 MPa @Temperature 23.0 °C	31200 psi @Temperature 73.4 °F	Absolute Drying; ASTM-D638
	250 MPa @Temperature -40.0 °C	36300 psi @Temperature -40.0 °F	Practical Use (Water Absorption 1.25%); ASTM-D638
	280 MPa @Temperature -40.0 °C	40600 psi @Temperature -40.0 °F	Absolute Drying; ASTM-D638
Elongation at Break	2.0 %	2.0 %	Absolute Drying; ASTM-D638
	2.2 %	2.2 %	Practical Use (Water Absorption 1.25%); ASTM-D638
Flexural Strength	175 MPa @Temperature 80.0 °C	25400 psi @Temperature 176 °F	Practical Use (Water Absorption 1.25%); ASTM-D790
	210 MPa @Temperature 80.0 °C	30500 psi @Temperature 176 °F	Absolute Drying; ASTM-D790
	260 MPa @Temperature 23.0 °C	37700 psi @Temperature 73.4 °F	Practical Use (Water Absorption 1.25%); ASTM-D790
	305 MPa @Temperature 23.0 °C	44200 psi @Temperature 73.4 °F	Absolute Drying; ASTM-D790
	310 MPa @Temperature -40.0 °C	45000 psi @Temperature -40.0 °F	Practical Use (Water Absorption 1.25%); ASTM-D790
	335 MPa @Temperature -40.0 °C	48600 psi @Temperature -40.0 °F	Absolute Drying; ASTM-D790
Flexural Modulus	6.60 GPa @Temperature 80.0 °C	957 ksi @Temperature 176 °F	Practical Use (Water Absorption 1.25%); ASTM-D790
	7.90 GPa @Temperature 80.0 °C	1150 ksi @Temperature 176 °F	Absolute Drying; ASTM-D790
	10.0 GPa @Temperature 23.0 °C	1450 ksi @Temperature 73.4 °F	Practical Use (Water Absorption 1.25%); ASTM-D790
	12.5 GPa @Temperature 23.0 °C	1810 ksi @Temperature 73.4 °F	Absolute Drying; ASTM-D790
	13.0 GPa @Temperature -40.0 °C	1890 ksi @Temperature -40.0 °F	Practical Use (Water Absorption 1.25%); ASTM-D790
	14.0 GPa @Temperature -40.0 °C	2030 ksi @Temperature -40.0 °F	Absolute Drying; ASTM-D790
Izod Impact, Notched	1.10 J/cm @Temperature -40.0 °C	2.06 ft-lb/in @Temperature -40.0 °F	Absolute Drying; ASTM-D256
	1.20 J/cm @Temperature -40.0 °C	2.25 ft-lb/in @Temperature -40.0 °F	Practical Use (Water Absorption 1.25%); ASTM-D256
	1.50 J/cm @Temperature 23.0 °C	2.81 ft-lb/in @Temperature 73.4 °F	Absolute Drying; ASTM-D256
	1.80 J/cm @Temperature 23.0 °C	3.37 ft-lb/in @Temperature 73.4 °F	Practical Use (Water Absorption 1.25%); ASTM-D256

Thermal Properties	Metric	English	Comments
CTE, linear	19.0 µm/m-°C	10.6 µin/in-°F	Absolute Drying; ASTM-D696
Deflection Temperature at 0.46 MPa (66 psi)	262 °C	504 °F	Absolute Drying; ASTM-D648
Deflection Temperature at 1.8 MPa (264 psi)	255 °C	491 °F	Absolute Drying; ASTM-D648
Flammability, UL94	HB	HB

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+10 ohm-cm	1.00e+10 ohm-cm	Practical Use (Water Absorption 1.25%); ASTM-D257
	1.00e+12 ohm-cm	1.00e+12 ohm-cm	Absolute Drying; ASTM-D257
Dielectric Strength	21.0 kV/mm @Thickness 2.00 mm	533 kV/in @Thickness 0.0787 in	Practical Use (Water Absorption 1.25%); ASTM-D149
	28.0 kV/mm @Thickness 2.00 mm	711 kV/in @Thickness 0.0787 in	Absolute Drying; ASTM-D149
Arc Resistance	93 sec	93 sec	Practical Use (Water Absorption 1.25%); ASTM-D495
	100 sec	100 sec	Absolute Drying; ASTM-D495
Comparative Tracking Index	550 V	550 V	IEC Method

Processing Properties	Metric	English
Melt Temperature	280 - 310 °C	536 - 590 °F
Mold Temperature	60.0 °C	140 °F
Injection Pressure	30.0 - 60.0 MPa	4350 - 8700 psi