Toyobo GLAMIDE® T-521 Nylon-6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced |
| Manufacturer | Toyobo |
| Trade Name | GLAMIDE® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo GLAMIDE® T-521 Nylon-6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade T-521 is a GF/mineral reinforced Nylon-6. It has high rigidity and good dimensional accuracy.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.37 g/cc | 1.37 g/cc | Absolute Drying; ASTM-D792 |
| Filler Content | 30 % | 30 % | |
| Water Absorption | 1.1 % | 1.1 % | Absolute Drying; ASTM-D570 |
| Moisture Absorption at Equilibrium | 2.5 % | 2.5 % | Absolute Drying; ASTM-D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm @Thickness 1.00 mm |
0.0020 - 0.0040 in/in @Thickness 0.0394 in |
Absolute Drying |
| 0.0040 - 0.0070 cm/cm @Thickness 3.00 mm |
0.0040 - 0.0070 in/in @Thickness 0.118 in |
Absolute Drying | |
| Melt Flow | 15 g/10 min | 15 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | Absolute Drying; ASTM-D785 |
| Tensile Strength, Ultimate | 42.0 MPa @Temperature 80.0 °C |
6090 psi @Temperature 176 °F |
Practical Use (Water Absorption 2.5%); ASTM-D638 |
| 56.0 MPa @Temperature 80.0 °C |
8120 psi @Temperature 176 °F |
Absolute Drying; ASTM-D638 | |
| 77.0 MPa @Temperature 23.0 °C |
11200 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.5%); ASTM-D638 | |
| 132 MPa @Temperature 23.0 °C |
19100 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D638 | |
| 135 MPa @Temperature -40.0 °C |
19600 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.5%); ASTM-D638 | |
| 158 MPa @Temperature -40.0 °C |
22900 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D638 | |
| Elongation at Break | 3.8 % | 3.8 % | Absolute Drying; ASTM-D638 |
| 5.8 % | 5.8 % | Practical Use (Water Absorption 2.5%); ASTM-D638 | |
| Flexural Strength | 70.0 MPa @Temperature 80.0 °C |
10200 psi @Temperature 176 °F |
Practical Use (Water Absorption 2.5%); ASTM-D790 |
| 105 MPa @Temperature 23.0 °C |
15200 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.5%); ASTM-D790 | |
| 120 MPa @Temperature 80.0 °C |
17400 psi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 130 MPa @Temperature -40.0 °C |
18900 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.5%); ASTM-D790 | |
| 180 MPa @Temperature 23.0 °C |
26100 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 245 MPa @Temperature -40.0 °C |
35500 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Flexural Modulus | 2.80 GPa @Temperature 80.0 °C |
406 ksi @Temperature 176 °F |
Practical Use (Water Absorption 2.5%); ASTM-D790 |
| 3.10 GPa @Temperature 80.0 °C |
450 ksi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 3.80 GPa @Temperature 23.0 °C |
551 ksi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.5%); ASTM-D790 | |
| 6.70 GPa @Temperature 23.0 °C |
972 ksi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 7.20 GPa @Temperature -40.0 °C |
1040 ksi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.5%); ASTM-D790 | |
| 8.40 GPa @Temperature -40.0 °C |
1220 ksi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Compressive Strength | 125 MPa | 18100 psi | Absolute Drying; ASTM-D695 |
| Izod Impact, Notched | 0.400 J/cm @Temperature -40.0 °C |
0.749 ft-lb/in @Temperature -40.0 °F |
Absolute Drying; ASTM-D256 |
| 0.650 J/cm @Temperature 23.0 °C |
1.22 ft-lb/in @Temperature 73.4 °F |
Absolute Drying; ASTM-D256 | |
| 0.700 J/cm @Temperature -40.0 °C |
1.31 ft-lb/in @Temperature -40.0 °F |
Practical Use (Water Absorption 2.5%); ASTM-D256 | |
| 1.85 J/cm @Temperature 23.0 °C |
3.47 ft-lb/in @Temperature 73.4 °F |
Practical Use (Water Absorption 2.5%); ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 24.0 µm/m-°C | 13.3 µin/in-°F | Absolute Drying; ASTM-D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 217 °C | 423 °F | Absolute Drying; ASTM-D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | Absolute Drying; ASTM-D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+9 ohm-cm | 1.00e+9 ohm-cm | Practical Use (Water Absorption 2.5%); ASTM-D257 |
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Absolute Drying; ASTM-D257 | |
| Dielectric Strength | 20.0 kV/mm @Thickness 2.00 mm |
508 kV/in @Thickness 0.0787 in |
Practical Use (Water Absorption 2.5%); ASTM-D149 |
| 26.0 kV/mm @Thickness 2.00 mm |
660 kV/in @Thickness 0.0787 in |
Absolute Drying; ASTM-D149 | |
| Arc Resistance | 100 sec | 100 sec | Practical Use (Water Absorption 2.5%); ASTM-D495 |
| 120 sec | 120 sec | Absolute Drying; ASTM-D495 | |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | |
| Mold Temperature | 60.0 °C | 140 °F | |
| Injection Pressure | 30.0 - 60.0 MPa | 4350 - 8700 psi |