Toyobo GLAMIDE® T-222SA Nylon/Elastomer
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Toyobo |
| Trade Name | GLAMIDE® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo GLAMIDE® T-222SA Nylon/Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade T-222SA is a super tough, non-reinforced alloy of nylon and elastomer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | Absolute Drying; ASTM-D792 |
| Water Absorption | 0.60 % | 0.60 % | Absolute Drying; ASTM-D570 |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | Absolute Drying; ASTM-D570 |
| Linear Mold Shrinkage | 0.0090 - 0.012 cm/cm @Thickness 1.00 mm |
0.0090 - 0.012 in/in @Thickness 0.0394 in |
Absolute Drying |
| 0.018 - 0.023 cm/cm @Thickness 3.00 mm |
0.018 - 0.023 in/in @Thickness 0.118 in |
Absolute Drying | |
| Melt Flow | 6.0 g/10 min | 6.0 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 85 | 85 | Absolute Drying; ASTM-D785 |
| Tensile Strength, Ultimate | 6.00 MPa @Temperature 80.0 °C |
870 psi @Temperature 176 °F |
Practical Use (Water Absorption 2.0%); ASTM-D638 |
| 8.00 MPa @Temperature 80.0 °C |
1160 psi @Temperature 176 °F |
Absolute Drying; ASTM-D638 | |
| 16.0 MPa @Temperature 23.0 °C |
2320 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.0%); ASTM-D638 | |
| 25.0 MPa @Temperature 23.0 °C |
3630 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D638 | |
| 45.0 MPa @Temperature -40.0 °C |
6530 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.0%); ASTM-D638 | |
| 50.0 MPa @Temperature -40.0 °C |
7250 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D638 | |
| Elongation at Break | 200 % | 200 % | Absolute Drying; ASTM-D638 |
| >= 200 % | >= 200 % | Practical Use (Water Absorption 2.0%); ASTM-D638 | |
| Flexural Strength | 6.00 MPa @Temperature 80.0 °C |
870 psi @Temperature 176 °F |
Practical Use (Water Absorption 2.0%); ASTM-D790 |
| 8.00 MPa @Temperature 80.0 °C |
1160 psi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 17.0 MPa @Temperature 23.0 °C |
2470 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.0%); ASTM-D790 | |
| 25.0 MPa @Temperature 23.0 °C |
3630 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 45.0 MPa @Temperature -40.0 °C |
6530 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.0%); ASTM-D790 | |
| 50.0 MPa @Temperature -40.0 °C |
7250 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Flexural Modulus | 0.100 GPa @Temperature 80.0 °C |
14.5 ksi @Temperature 176 °F |
Practical Use (Water Absorption 2.0%); ASTM-D790 |
| 0.200 GPa @Temperature 80.0 °C |
29.0 ksi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 0.400 GPa @Temperature 23.0 °C |
58.0 ksi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.0%); ASTM-D790 | |
| 0.700 GPa @Temperature 23.0 °C |
102 ksi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 1.20 GPa @Temperature -40.0 °C |
174 ksi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.0%); ASTM-D790 | |
| 1.40 GPa @Temperature -40.0 °C |
203 ksi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Izod Impact, Notched | 3.00 J/cm @Temperature -40.0 °C |
5.62 ft-lb/in @Temperature -40.0 °F |
Absolute Drying; ASTM-D256 |
| 3.20 J/cm @Temperature -40.0 °C |
5.99 ft-lb/in @Temperature -40.0 °F |
Practical Use (Water Absorption 2.0%); ASTM-D256 | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Practical Use (Water Absorption 2.0%); ASTM-D256 | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Absolute Drying; ASTM-D256 | |
| Taber Abrasion, mg/1000 Cycles | 8.0 | 8.0 | CS-17, Absolute Drying; ASTM-D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C | 50.0 µin/in-°F | Absolute Drying; ASTM-D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | Absolute Drying; ASTM-D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+9 ohm-cm | 1.00e+9 ohm-cm | Practical Use (Water Absorption 2.0%); ASTM-D257 |
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Absolute Drying; ASTM-D257 | |
| Dielectric Strength | 15.0 kV/mm @Thickness 2.00 mm |
381 kV/in @Thickness 0.0787 in |
Practical Use (Water Absorption 2.0%); ASTM-D149 |
| 18.0 kV/mm @Thickness 2.00 mm |
457 kV/in @Thickness 0.0787 in |
Absolute Drying; ASTM-D149 | |
| Arc Resistance | 115 sec | 115 sec | Practical Use (Water Absorption 2.0%); ASTM-D495 |
| 125 sec | 125 sec | Absolute Drying; ASTM-D495 | |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 300 °C | 500 - 572 °F | |
| Mold Temperature | 50.0 - 70.0 °C | 122 - 158 °F | |
| Injection Pressure | 50.0 - 80.0 MPa | 7250 - 11600 psi |
Users viewing this material also viewed the following:
- Global GPP-2000 Polypropylene Impact Copolymer, Cold Temperature Impact Resistant, Nucleated
- Stir SpA AF 80 3 IK (PVC)
- SABIC Innovative Plastics LNP Thermocomp KF002A Acetal Homopolymer (Asia Pacific)
- SABIC Innovative Plastics LNP THERMOCOMP QF007 PA 6/10 (Asia Pacific)
- A. Schulman POLYFORT™ FPP 1602 Glass Reinforced, Chemically Coupled Homopolymer
- Dow Corning CE 0101 WIPES LOTION
- Eurostar Staramide AG6ST43 PA66, 30% Glass Fiber Filled, Impact Modified, Injection Molded
- Fainplast Compounds HAX HF 22 Halogen Free PVC
- ConocoPhillips Hydroclear® 50 Power-D E.O. 50
Copyright © lookpolymers.com All Rights Reserved