Total Xsene® XS10 H HDPE, pipe, injection molding

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Pipe Grade
Manufacturer Total Atofina
Trade Name XSene®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total Xsene® XS10 H HDPE, pipe, injection molding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FINATHENE® XS 10 H is a high density polyethylene based on C6 hexene as co-monomer and is produced by the Fina Double Loop Technology™. FINATHENE® XS 10 H is a high performance dark blue compound specially developed for potable water distribution. FINATHENE® XS 10 H has a broad bimodal molecular weight distribution that ensures easy processing during extrusion. Due to its high melt strength, FINATHENE® XS 10 H is particularly suited for extrusion of large diameter, thick wall pipes.Information provided provided by Total Petrochemicals.Total Petrochemicals acquired former Fina and Atofina plastics product lines.
Physical Properties Metric English Comments
Density 0.950 g/cc
0.0343 lb/in³
ISO 1183
Viscosity 270000 cP

@Shear Rate 1000 1/s,
Temperature 190 °C
270000 cP

@Shear Rate 1000 1/s,
Temperature 374 °F
ATOFINA research test
2.10e+6 cP

@Shear Rate 100 1/s,
Temperature 190 °C
2.10e+6 cP

@Shear Rate 100 1/s,
Temperature 374 °F
ATOFINA research test
Oxidative Induction Time (OIT) >= 20 min
>= 20 min
200°C; EN 728
>= 20 min
>= 20 min
210°C; EN 728
Melt Flow 0.30 g/10 min

@Load 5.00 kg
0.30 g/10 min

@Load 11.0 lb
ISO 1133
High Load Melt Index 8.0 g/10 min

@Load 21.6 kg
8.0 g/10 min

@Load 47.6 lb
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 35.0 MPa
5080 psi
ISO 527
Tensile Strength, Yield 26.0 MPa
3770 psi
Elongation at Break >= 700 %
>= 700 %
ISO 527
Elongation at Yield 9.0 %
9.0 %
ISO 527
Flexural Modulus 1.25 GPa
181 ksi
ISO 178
Thermal Properties Metric English Comments
Specific Heat Capacity 2.00 J/g-°C
0.478 BTU/lb-°F
DSC
2.60 J/g-°C

@Temperature 150 °C
0.621 BTU/lb-°F

@Temperature 302 °F
DSC
Thermal Conductivity 0.400 W/m-K
2.78 BTU-in/hr-ft²-°F
DIN 52612
0.200 W/m-K

@Temperature 150 °C
1.39 BTU-in/hr-ft²-°F

@Temperature 302 °F
DIN 52612
Melting Point 130 - 132 °C
266 - 270 °F
crystalline; DSC