Total PPH 9081 Polypropylene, Homopolymer

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer Total Atofina
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total PPH 9081 Polypropylene, Homopolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ATOFINA Polypropylene PPH 9081 is a controlled-rheology homopolymer. PPH 9081 is characterized by a narrow molecular weight distribution and excellent flow properties, providing improved impact resistance and very low warpage for injection.ApplicationATOFINA Polypropylene PPH 9081 is particularly designed for the injection molding of thin walled articles and has good hinge properties.Information provided provided by Total Petrochemicals.Total Petrochemicals acquired former Fina and Atofina plastics product lines.
Physical Properties Metric English Comments
Bulk Density 0.525 g/cc
0.0190 lb/in³
ISO 1183
Density 0.905 g/cc
0.0327 lb/in³
ISO 1183
Melt Flow 25 g/10 min

@Load 2.16 kg,
Temperature 230 °C
25 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 92
92
ISO 2039-2
Tensile Strength, Yield 30.0 MPa
4350 psi
ISO 527-2
Elongation at Yield 10 %
10 %
ISO 527-2
Tensile Modulus 1.35 GPa
196 ksi
ISO 527-2
Flexural Modulus 1.25 GPa
181 ksi
ISO 527-2
Izod Impact, Notched (ISO) 3.50 kJ/m²
1.67 ft-lb/in²
ISO 179
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
Melting Point 165 °C
329 °F
ISO 3146
Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C
203 °F
120°C per hour; ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 52.0 °C
126 °F
120°C per hour; ISO 75-2
Vicat Softening Point 80.0 °C
176 °F
50N-50°C per hour; ISO 306
148 °C
298 °F
10N-50°C per hour; ISO 306