Total PPH 3762 Polypropylene, Extrusion Grade

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Fiber Grade
Manufacturer Total Atofina
Trade Name PPH
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total PPH 3762 Polypropylene, Extrusion Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Homopolymer fiber grade for staple fiber and multifilament yarnsFading Resistance - FINA 3762 is formulated to resist gas fading while maintaining excellent processing stability up to 250oC.Process Stability - FINA 3762 features excellent processability and the good physical properties necessary for fibers and multifilaments.FDA - FINA 3762 complies with all applicable FDA regulations for food contact.Recommended Applications - FINA 3762 is recommended for staple fibers and bulk continuous filament (BCF) yarns.Processing - FINA 3762 resin processes on conventional extrusion equipment with typical melt temperatures of 400-480°F (204- 250°C)Data provided by the manufacturer, Total Petrochemicals.Total Petrochemicals acquired former Fina and Atofina plastics product lines.
Physical Properties Metric English Comments
Density 0.905 g/cc
0.0327 lb/in³
ASTM D1505
Melt Flow 18 g/10 min
18 g/10 min
ASTM D1238L
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 250 MPa
36300 psi
Fiber value estimated from tenacity; ASTM D3218
Elongation at Break 65 %
65 %
Fiber property, 1.5 dpf multifilament. ASTM D3218
Modulus of Elasticity 1.65 GPa
239 ksi
ASTM D638
Tenacity 0.282 N/tex
3.20 g/denier
ASTM D3218
Flexural Modulus 1.515 GPa
219.7 ksi
Flexural modulus is 1.515 GPa. Flexural stiffness is 1.215 GPa. ASTM D790
Thermal Properties Metric English Comments
Melting Point 165 °C
329 °F
DSC
Deflection Temperature at 0.46 MPa (66 psi) 115 °C
239 °F
Vicat Softening Point 150 - 155 °C
302 - 311 °F
Softening point range is 150-155°C. Method not specified.
Processing Properties Metric English Comments
Melt Temperature 204 - 250 °C
399 - 482 °F
Extrusion