Material Notes:
ATOFINA Propylene 9642 is nucleated heterophasic copolymer. PPC 9642 is characterized by improved stiffness, creep resistance, high impact resistance, excellent antistatic properties and has been formulated to allow faster cycling through early demolding.
Physical Properties Metric English Comments
Bulk Density 0.525 g/cc
0.0190 lb/in³
ISO 1183
Density 0.905 g/cc
0.0327 lb/in³
ISO 1183
Melt Flow 25 g/10 min

@Load 2.16 kg,
Temperature 230 °C
25 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 87
87
ISO 2039-2
Tensile Strength, Yield 28.0 MPa
4060 psi
ISO 527-2
Elongation at Yield 5.5 %
5.5 %
ISO 527-2
Tensile Modulus 1.60 GPa
232 ksi
ISO 527-2
Flexural Modulus 1.50 GPa
218 ksi
ISO 527-2
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
ISO 179
5.00 kJ/m²

@Temperature -20.0 °C
2.38 ft-lb/in²

@Temperature -4.00 °F
ISO 179
Charpy Impact, Notched 0.550 J/cm²
2.62 ft-lb/in²
ISO 179
0.900 J/cm²

@Temperature -20.0 °C
4.28 ft-lb/in²

@Temperature -4.00 °F
ISO 179
Thermal Properties Metric English Comments
Melting Point 165 °C
329 °F
ISO 3146
Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C
203 °F
120°C per hour; ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 53.0 °C
127 °F
120°C per hour; ISO 75-2
Vicat Softening Point 75.0 °C
167 °F
50N-50°C per hour; ISO 306
145 °C
293 °F
10N-50°C per hour; ISO 306