- HOME
- POLYMER SEARCH
- Thermoplastic
- Polypropylene (PP)
- Polypropylene, Molded
- Total PPC 3650 Polypropylene, Heterophasic Copolymer, Injection Molding
Total PPC 3650 Polypropylene, Heterophasic Copolymer, Injection Molding
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | Total Atofina |
| Trade Name | PPC |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Total PPC 3650 Polypropylene, Heterophasic Copolymer, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polypropylene PPC 3650 is a heterophasic copolymer with a Melt Flow index of 2 g/10 min.Polypropylene PPC 3650 provides an excellent balance between toughness and flow, being particularly suitable in injection molding for heavy duty applications such as tote bins, bread and vegetable trays, crates and large pails.Information provided by Total Petrochemicals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.905 g/cc | 0.905 g/cc | ISO 1183 |
| Bulk Density | 0.525 g/cc | 0.0190 lb/in³ | ISO 1183 |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 78 | 78 | ISO 2039-2 |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | ISO 527-2 |
| Elongation at Yield | 11 % | 11 % | ISO 527-2 |
| Tensile Modulus | 1.25 GPa | 181 ksi | ISO 527-2 |
| Flexural Modulus | 1.15 GPa | 167 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 6.50 kJ/m² @Temperature -20.0 °C |
3.09 ft-lb/in² @Temperature -4.00 °F |
ISO 180 |
| >= 50.0 kJ/m² @Temperature 23.0 °C |
>= 23.8 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |
| Charpy Impact, Notched | 0.750 J/cm² @Temperature -20.0 °C |
3.57 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| >= 5.00 J/cm² @Temperature 23.0 °C |
>= 23.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | ISO 3146 |
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | 120°C per hour; ISO 752 |
| Deflection Temperature at 1.8 MPa (264 psi) | 48.0 °C | 118 °F | 120°C per hour; ISO 752 |
| Vicat Softening Point | 65.0 °C @Load 5.10 kg |
149 °F @Load 11.2 lb |
50°C per hour; ISO 306 |
| 147 °C @Load 1.02 kg |
297 °F @Load 2.25 lb |
50°C per hour; ISO 306 |