Total PPC 11812 S01 Polypropylene, Heterophasic Copolymer, Injection Molding

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded
Manufacturer	Total Atofina
Trade Name	PPC
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Total PPC 11812 S01 Polypropylene, Heterophasic Copolymer, Injection Molding.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Polypropylene PPC 11812 S01 has been developed for high speed injection molding of thin walled packaging containers requiring top level impact resistance at cold temperature (-20°C). It is characterized by a high Melt Flow index of 50 g/10 min, and allows an optimization of the injection parameters as for example a reduction of the cycle time, while keeping properties even at cold temperature (impact).Information provided by Total Petrochemicals.

Physical Properties	Metric	English	Comments
Specific Gravity	0.905 g/cc	0.905 g/cc	ISO 1183
Bulk Density	0.525 g/cc	0.0190 lb/in³	ISO 1183
Melt Flow	50 g/10 min @Load 2.16 kg, Temperature 230 °C	50 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	24.0 MPa	3480 psi	ISO 527-2
Elongation at Yield	5.0 %	5.0 %	ISO 527-2
Tensile Modulus	1.15 GPa	167 ksi	ISO 527-2
Flexural Modulus	1.10 GPa	160 ksi	ISO 178
Izod Impact, Notched (ISO)	6.50 kJ/m² @Temperature -20.0 °C	3.09 ft-lb/in² @Temperature -4.00 °F	ISO 180
	13.5 kJ/m² @Temperature 23.0 °C	6.42 ft-lb/in² @Temperature 73.4 °F	ISO 180

Thermal Properties	Metric	English	Comments
Melting Point	165 °C	329 °F	ISO 3146
Deflection Temperature at 0.46 MPa (66 psi)	90.0 °C	194 °F	120°C per hour; ISO 752
Deflection Temperature at 1.8 MPa (264 psi)	48.0 °C	118 °F	120°C per hour; ISO 752
Vicat Softening Point	70.0 °C @Load 5.10 kg	158 °F @Load 11.2 lb	50°C per hour; ISO 306
	140 °C @Load 1.02 kg	284 °F @Load 2.25 lb	50°C per hour; ISO 306