Total Lumicene® mPE M 2704 EP S01 Metallocene Polyethylene, Blown Film

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Hexene, Film Grade
Manufacturer Total Atofina
Trade Name Lumicene®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total Lumicene® mPE M 2704 EP S01 Metallocene Polyethylene, Blown Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This product is a Total Ecosolutions grade.Lumicene® mPE M 2704 EP S01 is a second generation metallocene based Low Density Polyethylene with hexene as comonomer.Lumicene® mPE M 2704 EP S01 can be processed at high output rates with excellent bubble stability and gauge control in comparison with conventional LLDPE and first generation metallocene based polyethylene. The combination of these features brings a significant downgauging potential.Lumicene® mPE M 2704 EP S01 is suited for many applications in the field of consumer and industrial packaging, collation and industrial shrink as well as agricultural film.Information provided by Total Petrochemicals.
Physical Properties Metric English Comments
Specific Gravity 0.927 g/cc
0.927 g/cc
ISO 1183
Thickness 40.0 microns
1.57 mil
Melt Flow 0.35 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.35 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 14.5 MPa
2100 psi
ISO 527-3
Film Tensile Strength at Yield, TD 15.0 MPa
2180 psi
ISO 527-3
Film Elongation at Break, MD 640 %
640 %
ISO 527-3
Film Elongation at Break, TD 710 %
710 %
ISO 527-3
Elmendorf Tear Strength, MD 4.10 g/micron
104 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 15.3 g/micron
389 g/mil
ISO 6383-2
Dart Drop Test 220 g
0.485 lb
ISO 7765-1
Film Tensile Strength at Break, MD 65.0 MPa
9430 psi
ISO 527-3
Film Tensile Strength at Break, TD 57.0 MPa
8270 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 121 °C
250 °F
ISO 11357
Vicat Softening Point 119 °C
246 °F
ISO 306
Optical Properties Metric English Comments
Haze 8.0 %
8.0 %
ISO 14782
Gloss 65 %
65 %
at 45°; ASTM D2457
Processing Properties Metric English Comments
Processing Temperature 180 - 230 °C
356 - 446 °F
Blow Molding
Melt Temperature 200 °C
392 °F
Extrusion
Die Opening 0.120 - 0.280 cm
0.0472 - 0.110 in
Blow-up Ratio (BUR) 1.5 - 4.5
1.5 - 4.5