Total L425 HDPE Film

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , MDPE , Medium Density Polyethylene (MDPE), Film Grade
Manufacturer Total Atofina
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total L425 HDPE Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Blown film polyethylene grade. Provides excellent bubble stability, exceptional tear strength, high impact and puncture resistance, outstanding clarity and gloss, good stiffness, excellent compatibility with LDPE and LLDPE..Applications: L425 is recommended for shrink films, heavy duty sacks, food packaging, laminations and multilayer packaging film.Information provided provided by Total Petrochemicals.
Physical Properties Metric English Comments
Density 0.925 g/cc
0.0334 lb/in³
ASTM D792
Thickness 25.4 microns
1.00 mil
as tested; BUR 2.5
Melt Flow 0.40 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.40 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
High Load Melt Index 12 g/10 min

@Load 21.6 kg,
Temperature 190 °C
12 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 700 %

@Thickness 0.0254 mm
700 %

@Thickness 0.00100 in
ASTM D882A
Film Elongation at Break, TD 800 %

@Thickness 0.0254 mm
800 %

@Thickness 0.00100 in
ASTM D882A
Elmendorf Tear Strength MD 250 g

@Thickness 0.0254 mm
250 g

@Thickness 0.00100 in
ASTM D1922
Elmendorf Tear Strength TD 800 g

@Thickness 0.0254 mm
800 g

@Thickness 0.00100 in
ASTM D1922
Dart Drop 11.8 g/micron

@Thickness 0.0254 mm
300 g/mil

@Thickness 0.00100 in
ASTM D1709A
Dart Drop Test 300 g
0.662 lb
1.0 mil; ASTM D 1709
Film Tensile Strength at Break, MD 37.9 MPa

@Thickness 0.0254 mm
5500 psi

@Thickness 0.00100 in
ASTM D882A
Film Tensile Strength at Break, TD 34.5 MPa

@Thickness 0.0254 mm
5000 psi

@Thickness 0.00100 in
ASTM D882A
1% Secant Modulus, MD 179 MPa

@Thickness 0.0254 mm
26000 psi

@Thickness 0.00100 in
ASTM D882A
1% Secant Modulus, TD 186 MPa

@Thickness 0.0254 mm
27000 psi

@Thickness 0.00100 in
ASTM D882A
Thermal Properties Metric English Comments
Melting Point 120 °C
248 °F
ASTM D3417
Descriptive Properties Value Comments
Process Film
Region US & Canada
Bamberger Polymers Distribution