Total EVA 1005 VN 35 Ethylene Vinyl Acetate Copolymer - Blown Film

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer Total Atofina
Trade Name EVA
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total EVA 1005 VN 35 Ethylene Vinyl Acetate Copolymer - Blown Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
EVA 1005 VN 35 is made by a high pressure tubular process. Grade for flexible films, with high transparency and outstanding mechanical properties. Contains NO antioxidant.Information provided by Total Petrochemicals.
Physical Properties Metric English Comments
Specific Gravity 0.935 g/cc
0.935 g/cc
ISO 1183
Vinyl Acetate Content 12 %
12 %
Thickness 40.0 microns
1.57 mil
for samples tested on this data sheet
30.0 - 200 microns
1.18 - 7.87 mil
possible range, depending on extrusion conditions
Melt Flow 0.50 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.50 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 6.40 MPa
928 psi
ISO 527-3
Film Tensile Strength at Yield, TD 5.60 MPa
812 psi
ISO 527-3
Film Elongation at Break, MD 380 %
380 %
ISO 527-3
Film Elongation at Break, TD 650 %
650 %
ISO 527-3
Modulus of Elasticity 0.0700 GPa
10.2 ksi
ISO 527-2
Elmendorf Tear Strength, MD 1.50 g/micron
38.1 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 2.00 g/micron
50.8 g/mil
ISO 6383-2
Dart Drop Test 630 g
1.39 lb
ISO 7765-1
Film Tensile Strength at Break, MD 39.0 MPa
5660 psi
ISO 527-3
Film Tensile Strength at Break, TD 37.0 MPa
5370 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 91.0 °C
196 °F
ISO 11357
Vicat Softening Point 72.0 °C
162 °F
ISO 306
Optical Properties Metric English Comments
Haze 4.4 %
4.4 %
ISO 14782
Processing Properties Metric English Comments
Processing Temperature 150 - 180 °C
302 - 356 °F