Total 6410 HDPE Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer Total Atofina
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total 6410 HDPE Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Unique combination of high stiffness and clarity; Good moisture barrier properties; Good processability; Good compatibility with LDPE and LLDPEApplications: paper overwrap, cup overwrap, plate overwrap, envelope windows, release liners, stand-up bags, specialty monolayer films, coextruded filmsInformation provided provided by Total Petrochemicals.
Physical Properties Metric English Comments
Density 0.961 g/cc
0.0347 lb/in³
ASTM D 792
Water Vapor Transmission 9.31 g/m²/day
0.600 g/100 in²/day
100°F; E 96/66
Thickness 25.4 microns
1.00 mil
Melt Flow 1.2 g/10 min

@Load 2.16 kg
1.2 g/10 min

@Load 4.76 lb
ASTM D 1238
High Load Melt Index 33 g/10 min

@Load 21.6 kg
33 g/10 min

@Load 47.6 lb
ASTM D 1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 26.2 MPa
3800 psi
ASTM D 882 A
Film Tensile Strength at Yield, TD >= 27.6 MPa
>= 4000 psi
ASTM D 882 A
Film Elongation at Break, TD 700 %
700 %
ASTM D 882 A
Secant Modulus, MD 0.689 GPa
99.9 ksi
ASTM D 882 A
Secant Modulus, TD 0.703 GPa
102 ksi
ASTM D 882 A
Elmendorf Tear Strength MD 24 g
24 g
ASTM D 1922
Elmendorf Tear Strength TD 385 g
385 g
ASTM D 1922
Film Tensile Strength at Break, MD >= 51.7 MPa
>= 7500 psi
ASTM D 882 A
Film Tensile Strength at Break, TD >= 23.4 MPa
>= 3400 psi
ASTM D 882 A
Thermal Properties Metric English Comments
Melting Point 129 °C
265 °F
ASTM D3417
Optical Properties Metric English Comments
Haze 15 %
15 %
ASTM D 1003
Gloss 50 %
50 %
ASTM D 523
Descriptive Properties Value Comments
Process Film
Region US & Canada
Bamberger Polymers Distribution