Total 1285 HDPE film

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer Total Atofina
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total 1285 HDPE film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Applications: T-shirt sacks, trash can liners, merchandise bags, coex applicationsInformation provided provided by Total Petrochemicals.Total Petrochemicals acquired former Fina and Atofina plastics product lines.
Physical Properties Metric English Comments
Density 0.950 g/cc
0.0343 lb/in³
ISO 1183
Water Vapor Transmission 12.4 g/m²/day
0.799 g/100 in²/day
100°F
Thickness 20.3 microns
0.800 mil
Melt Flow 0.070 g/10 min

@Load 2.16 kg
0.070 g/10 min

@Load 4.76 lb
ISO 1133
0.31 g/10 min

@Load 5.00 kg
0.31 g/10 min

@Load 11.0 lb
ISO 1133
High Load Melt Index 9.0 g/10 min

@Load 21.6 kg
9.0 g/10 min

@Load 47.6 lb
ISO 1133
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD >= 36.5 MPa
>= 5300 psi
ASTM D 882 A
Film Tensile Strength at Yield, TD >= 34.5 MPa
>= 5000 psi
ASTM D 882 A
Film Elongation at Break, MD 300 - 500 %
300 - 500 %
ASTM D 882 A
Film Elongation at Break, TD 300 - 500 %
300 - 500 %
ASTM D 882 A
Secant Modulus, MD 0.841 GPa
122 ksi
ASTM D 882 A
Secant Modulus, TD 0.910 GPa
132 ksi
ASTM D 882 A
Elmendorf Tear Strength MD 24 g
24 g
ASTM D 1922
Elmendorf Tear Strength TD 120 g
120 g
ASTM D 1922
Dart Drop Test 350 g
0.772 lb
ASTM D 1709
Film Tensile Strength at Break, MD >= 61.4 MPa
>= 8900 psi
ASTM D 882 A
Film Tensile Strength at Break, TD >= 58.6 MPa
>= 8500 psi
ASTM D 882 A
Thermal Properties Metric English Comments
Melting Point 127 °C
260 °F
ASTM D3417