Topas Advanced Polymers TOPAS® 9903D-10 Cyclic Olefin Copolymer (COC)

Category Polymer , Thermoplastic , Cyclo Olefin Polymer
Manufacturer Topas Advanced Polymers
Trade Name TOPAS®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Topas Advanced Polymers TOPAS® 9903D-10 Cyclic Olefin Copolymer (COC).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TOPAS® 9903D-10 is a very low glass transition temperature (Tg=33°C) film extrusion grade. It is designed to deliver high shrinkage at low temperatures in shrink packaging applications. It is a moderate clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and general purpose applications. It is used in blends in monolayer products, and alone or in blends in multilayer films. It can be used in both cast and blown film processes. The leading film applications are shrink films and labels. Key applications and attributes: Shrink films and labels: High shrink at low temperatures, low stress, toughness Food packaging: Not manufactured with BPA, phthalates, or halogens Food contact: Broad regulatory approval Storage: This grade tends to stick due to its low glass transition temperature. This is also true for parts made thereof. Chilled warehousing is recommended. Information provided by TOPAS Advanced Polymers
Physical Properties Metric English Comments
Oxygen Permeability 1600 cm3 mil/(m2 day atm)
103 cm3 mil/(100 in2 day atm)
Water Vapor Permeability 7.60 g mil/ (m2 day)
0.490 g mil/ (100 in2 day)
Density 1.02 g/cc
0.0368 lb/in³
ISO 1183
Water Vapor Transmission 0.000190 g/m²/day

@Temperature 23.0 °C
0.0000122 g/100 in²/day

@Temperature 73.4 °F
85% RH; ISO 15106-3
Oxygen Transmission 0.0400 cc-mm/m²-24hr-atm

@Temperature 23.0 °C
0.102 cc-mil/100 in²-24hr-atm

@Temperature 73.4 °F
50% RH
Thickness 100 microns
3.94 mil
Melt Flow 0.92 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.92 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
3.7 g/10 min

@Load 2.16 kg,
Temperature 230 °C
3.7 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
7.4 g/10 min

@Load 2.16 kg,
Temperature 260 °C
7.4 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Elongation at Break, MD >= 150 %
>= 150 %
ISO 527-3
Film Elongation at Break, TD >= 100 %
>= 100 %
ISO 527-3
Tensile Modulus 1.26 GPa
183 ksi
Bar; ISO 527-3
Film Tensile Strength at Break, MD 25.0 MPa
3630 psi
ISO 527-3
Film Tensile Strength at Break, TD 22.0 MPa
3190 psi
ISO 527-3
Thermal Properties Metric English Comments
Glass Transition Temp, Tg 33.0 °C
91.4 °F
10°C/min; ISO 11357
Optical Properties Metric English Comments
Haze <= 1.0 %
<= 1.0 %
ISO 14782
Gloss >= 100 %
>= 100 %
60°
Descriptive Properties Value Comments