Topas Advanced Polymers TOPAS® 9506F-500 Cyclic Olefin Copolymer (COC)

Category Polymer , Thermoplastic , Cyclo Olefin Polymer
Manufacturer Topas Advanced Polymers
Trade Name TOPAS®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Topas Advanced Polymers TOPAS® 9506F-500 Cyclic Olefin Copolymer (COC).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TOPAS® 9506F-500 is a high clarity extrusion grade for use in shrink, food and medical packaging as either a discrete layer in multilayer film or in blends with polyethylene. It is designed to deliver high shrinkage at low temperatures in shrink packaging applications. It has low glass transition temperature and provides excellent clarity, stiffness, water vapor barrier and good thermoformability.Key applications and attributes: Shrink films and labels: High shrink at low temperatures, low stress, toughness Food packaging: Not manufactured with BPA, phthalates, or halogens Food contact: Broad regulatory approval Information provided by TOPAS Advanced Polymers
Physical Properties Metric English Comments
Oxygen Permeability 775 cm3 mil/(m2 day atm)

@Temperature 23.0 °C
50.0 cm3 mil/(100 in2 day atm)

@Temperature 73.4 °F
50% RH; ASTM D3985
Water Vapor Permeability 4.60 g mil/ (m2 day)

@Temperature 38.0 °C
0.297 g mil/ (100 in2 day)

@Temperature 100 °F
90% RH; ISO 15106-3
Density 1.02 g/cc
0.0368 lb/in³
ISO 1183
Water Absorption at Saturation 0.010 %

@Temperature 23.0 °C
0.010 %

@Temperature 73.4 °F
ISO 62
Thickness 70.0 microns
2.76 mil
Film
Melt Flow 0.92 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.92 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
5.5 g/10 min

@Load 2.16 kg,
Temperature 230 °C
5.5 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 2.9 %
2.9 %
ISO 527-3
Film Elongation at Break, TD 3.6 %
3.6 %
ISO 527-3
Tensile Modulus 1.70 GPa
247 ksi
Film, MD; ISO 527-3
2.00 GPa
290 ksi
Film, TD; ISO 527-3
Elmendorf Tear Strength MD 230 g
230 g
ISO 6383-2
Elmendorf Tear Strength TD 240 g
240 g
ISO 6383-2
Dart Drop Test <= 36.0 g
<= 0.0794 lb
F50; ISO 7765-1
Film Tensile Strength at Break, MD 55.0 MPa
7980 psi
ISO 527-3
Film Tensile Strength at Break, TD 55.0 MPa
7980 psi
ISO 527-3
Thermal Properties Metric English Comments
Glass Transition Temp, Tg 65.0 °C
149 °F
10°C/min; ISO 11357-1,-2,-3
Optical Properties Metric English Comments
Haze >= 2.0 %
>= 2.0 %
Film; ISO 14782
Gloss >= 100 %
>= 100 %
60°, Film; ISO 2813
Descriptive Properties Value Comments
Type of film extrusion Cast
Test specimen