Tisan TISLAMID® 6 25% Glass Fiber Reinforced Flame Retardant (V0). Heat Stabilized Nylon 6

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Fiber Filled, Flame Retardant
Manufacturer Tisan Engineering Plastics
Trade Name TISLAMID®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Tisan TISLAMID® 6 25% Glass Fiber Reinforced Flame Retardant (V0). Heat Stabilized Nylon 6.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TISLAMID has a wide area of application in electric/electronic, automotive, durable goods and telecommunications industries. It demonstrates characteristics such as Excellent chemical resistanceElectric isolationEasy processabilityHigh mechanical resistanceExcellent flame retardanceHigh moisture absorptionExcellent temperature resistanceHigh performance / affordable priceAbrasion resistanceTISLAMID has an excellent resistance to weak alkalis and organic solvents. It has a good resistance to weak acids, alcohols, hydrocarbons, and engine fuels. It has a medium resistance to strong alkalis and a weak resistance to strong acids.
Physical Properties Metric English Comments
Density 1.50 g/cc
0.0542 lb/in³
ISO 1183
Ash 25 %
25 %
ISO 3451
Mechanical Properties Metric English Comments
Tensile Strength at Break 105 MPa
15200 psi
ISO 527-2
Tensile Strength, Yield 110 MPa
16000 psi
ISO 527-2
Elongation at Break 3.0 %
3.0 %
ISO 527-2
Elongation at Yield 2.9 %
2.9 %
ISO 527-2
Modulus of Elasticity 7.50 GPa
1090 ksi
ISO 527-2
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
Melting Point 220 - 225 °C
428 - 437 °F
Flammability, UL94 V-0
V-0
Glow Wire Test 960 °C
1760 °F
60695-2-10
Electrical Properties Metric English Comments
Comparative Tracking Index 500 V
500 V
TS EN 60112
Processing Properties Metric English Comments
Feed Temperature 60.0 - 80.0 °C
140 - 176 °F
Rear Barrel Temperature 220 - 240 °C
428 - 464 °F
Aft-1. Region Temperature
Middle Barrel Temperature 220 - 240 °C
428 - 464 °F
Mid-2. Region Temperature
Front Barrel Temperature 220 - 240 °C
428 - 464 °F
Pre-3. Region Temperature
Nozzle Temperature 210 - 230 °C
410 - 446 °F
Melt Temperature 220 - 240 °C
428 - 464 °F
Drying Temperature 90.0 - 100 °C
194 - 212 °F
Predrying Temperature
Dry Time 3 - 4 hour
3 - 4 hour
Predrying Time
Descriptive Properties Value Comments
Block Temperature 60-80°C