Tisan TISARBON® Flame Retardant (V0) Polycarbonate

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant
Manufacturer Tisan Engineering Plastics
Trade Name TISARBON®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Tisan TISARBON® Flame Retardant (V0) Polycarbonate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TISARBON has a wide area of application in construction, building auxiliary materials, electric/electronic, lighting equipment, home appliances, automotive, telecommunication and health products industries. General Specifications include: High temperature resistanceDimensional stabilityImpact resistanceExcellent surface qualityHigh light transparenceFlame resistanceLow moisture ratioToughness TISARBON has good chemical resistance against weak acids. It has medium resistance against alcohols, hydrocarbons, and engine fuels, and weak resistance against acids, alkalis, and organic solvents.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
ISO 527-2
Tensile Strength, Yield 60.0 MPa
8700 psi
ISO 527-2
Elongation at Break 6.5 %
6.5 %
ISO 527-2
Elongation at Yield 5.0 %
5.0 %
ISO 527-2
Modulus of Elasticity 2.30 GPa
334 ksi
ISO 527-2
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
Melting Point 230 °C
446 °F
Vicat Softening Point 141 °C
286 °F
ISO 306
Heat Distortion Temperature 135 °C
275 °F
ISO 75-2
Flammability, UL94 V-0
V-0
Glow Wire Test 960 °C
1760 °F
60695-2-10
Processing Properties Metric English Comments
Feed Temperature 70.0 °C
158 °F
Rear Barrel Temperature 280 - 290 °C
536 - 554 °F
Aft-1. Region Temperature
Middle Barrel Temperature 270 - 280 °C
518 - 536 °F
Mid-2. Region Temperature
Front Barrel Temperature 260 - 270 °C
500 - 518 °F
Pre-3. Region Temperature
Nozzle Temperature 280 - 290 °C
536 - 554 °F
Melt Temperature 270 - 290 °C
518 - 554 °F
Drying Temperature 90.0 - 120 °C
194 - 248 °F
Predrying Temperature
Dry Time 3 - 5 hour
3 - 5 hour
Predrying Time
Moisture Content 0.20 %
0.20 %
ISO 62
Descriptive Properties Value Comments
Block Temperature 80°C