Thermal Ceramics TR-2000 Block Insulation

Category Ceramic
Manufacturer Thermal Ceramics
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Thermal Ceramics TR-2000 Block Insulation.pdf
  Online Service   lookpolymers   27660005
Material Notes:
TR-2000 SL Block Insulation is an asbestos-free insulation, manufactured from calcium silicate and reinforced with cellulose fibers. This item is versatile products available in a wide range of sizes with either beveled or straight edges.Because of its low conductivity, this board is economical, energy saving insulation. It exhibits minimal shrinkage at top temperature limits, and will not decompose at its maximum service temperature.Features:Very low thermal conductivityLightweightGood high-temperature strengthApplications:Tub wall insulating material in carbon baking pitsBackup insulation in aluminum pot cells Reheat and pusher furnacesGeneral backup insulationCommercial appliancesInformation provided by Thermal CeramicsData has not been recently verified. Please contact manufacturer for current information.
Physical Properties Metric English Comments
Density 0.280 g/cc
0.0101 lb/in³
at ambient temperature
Loss On Ignition 4.9 %
4.9 %
Porosity 90 %
90 %
Mechanical Properties Metric English Comments
Modulus of Rupture 0.00107 GPa
0.155 ksi
at ambient temperature
Compressive Strength 0.0103 MPa

@Temperature 577 °C
1.49 psi

@Temperature 1070 °F
Thermal Properties Metric English Comments
Thermal Conductivity 0.0800 W/m-K

@Temperature 260 °C
0.555 BTU-in/hr-ft²-°F

@Temperature 500 °F
0.100 W/m-K

@Temperature 540 °C
0.694 BTU-in/hr-ft²-°F

@Temperature 1000 °F
0.140 W/m-K

@Temperature 815 °C
0.972 BTU-in/hr-ft²-°F

@Temperature 1500 °F
0.160 W/m-K

@Temperature 980 °C
1.11 BTU-in/hr-ft²-°F

@Temperature 1800 °F
Maximum Service Temperature, Air 1050 °C
1922 °F
1090 °C
2000 °F
Shrinkage 1.00 %

@Temperature 1040 °C
1.00 %

@Temperature 1900 °F
Component Elements Properties Metric English Comments
CaO 46.2 %
46.2 %
Fe2O3 0.30 %
0.30 %
Other 4.9 %
4.9 %
SiO2 48.6 %
48.6 %