Ter Hell Plastic Terez® PA 6 7500 TF 20 GF 20 Polyamide 6, 20% PTFE chemically bonded 20% glass fiber reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, PTFE Filled
Manufacturer Ter Hell Plastic GMBH
Trade Name Terez®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ter Hell Plastic Terez® PA 6 7500 TF 20 GF 20 Polyamide 6, 20% PTFE chemically bonded 20% glass fiber reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Medium viscosity PA 6, 20% PTFE chemically bonded and 20% glass fiber reinforced, good flowability, good impact resistance and bright natural color.Application: For molding parts with increased stiffness and side loading.Information provided by Ter Hell Plastic GMBH.
Physical Properties Metric English Comments
Specific Gravity 1.42 g/cc
1.42 g/cc
ISO 1183
Water Absorption 5.7 %
5.7 %
ISO 62
Moisture Absorption at Equilibrium 1.5 %
1.5 %
ISO 62
Mechanical Properties Metric English Comments
Tensile Strength at Break 138 MPa
20000 psi
dry; ISO 527
Tensile Strength 140 MPa
20300 psi
dry; ISO 527
Tensile Strength, Yield 145 MPa
21000 psi
dry; ISO 527
Elongation at Break 3.0 %
3.0 %
dry; ISO 527
Elongation at Yield 2.0 %
2.0 %
dry; ISO 527
Tensile Modulus 6.80 GPa
986 ksi
dry; ISO 527
Charpy Impact Unnotched 8.00 J/cm²
38.1 ft-lb/in²
dry; ISO 179
Charpy Impact, Notched 1.20 J/cm²
5.71 ft-lb/in²
dry; ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
ISO 75
Vicat Softening Point 215 °C
419 °F
B/50; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Processing Properties Metric English Comments
Processing Temperature 240 - 270 °C
464 - 518 °F
Drying Temperature 90.0 °C
194 °F
Dry Time 5 - 6 hour
5 - 6 hour