Ter Hell Plastic Terez® 3610/4 PA/ABS Blend

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer	Ter Hell Plastic GMBH
Trade Name	Terez®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ter Hell Plastic Terez® 3610/4 PA/ABS Blend.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Impact resistant blend with reduced moisture absorption and good flowability.Application: For molding parts with increased demand of impact strength and cold impact strength. For injection molding.Information provided by Ter Hell Plastic GMBH.

Physical Properties	Metric	English	Comments
Specific Gravity	1.10 g/cc	1.10 g/cc	ISO 1183
Water Absorption	5.0 %	5.0 %	ISO 62
Moisture Absorption at Equilibrium	1.6 %	1.6 %	ISO 62
Melt Flow	30 g/10 min @Load 5.00 kg, Temperature 260 °C	30 g/10 min @Load 11.0 lb, Temperature 500 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength	58.0 MPa	8410 psi	dry; ISO 527
Elongation at Break	60 %	60 %	dry; ISO 527
Tensile Modulus	2.30 GPa	334 ksi	dry; ISO 527
Charpy Impact Unnotched	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	dry; ISO 179
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	dry; ISO 179
Charpy Impact, Notched	1.00 J/cm² @Temperature -30.0 °C	4.76 ft-lb/in² @Temperature -22.0 °F	dry; ISO 179
	3.00 J/cm² @Temperature 23.0 °C	14.3 ft-lb/in² @Temperature 73.4 °F	dry; ISO 179

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	125 °C	257 °F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	65.0 °C	149 °F	ISO 75
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in

Processing Properties	Metric	English
Processing Temperature	230 - 270 °C	446 - 518 °F
Drying Temperature	80.0 °C	176 °F
Dry Time	4 hour	4 hour