Teknor Apex Chemlon® 225-15 MG Nylon 6, 25% Mineral Reinforced, 15% Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled , Nylon 6, 30% Mineral Filled , Nylon 6, Glass Fiber Filled, Flame Retardant , Nylon 6, Glass/Mineral Reinforced |
| Manufacturer | Teknor Apex Company |
| Trade Name | Chemlon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teknor Apex Chemlon® 225-15 MG Nylon 6, 25% Mineral Reinforced, 15% Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Compound offering rigidity and strength, especially at high service temperatures; Excellent for large area parts Processing Method: Injection Molding Forms: Pellets Automotive Specifications: FORD ESB-M4D353-A3Information Provided by Teknor Apex
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.52 g/cc | 1.52 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0015 - 0.0040 cm/cm | 0.0015 - 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 128 MPa | 18500 psi | ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| Elongation at Yield | 2.5 % | 2.5 % | ASTM D638 |
| Flexural Strength | 190 MPa | 27500 psi | ASTM D790 |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D790 |
| Izod Impact, Notched | 0.854 J/cm @Temperature 22.8 °C |
1.60 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 55.8 µm/m-°C | 31.0 µin/in-°F | ASTM D696 |
| Melting Point | 216 °C | 420 °F | DSC |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | Unannealed; ASTM D648 |
| UL RTI, Electrical | 65.0 °C @Thickness 0.810 mm |
149 °F @Thickness 0.0319 in |
UL 746 |
| 65.0 °C @Thickness 1.50 mm |
149 °F @Thickness 0.0590 in |
UL 746 | |
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
UL 746 | |
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.810 mm |
149 °F @Thickness 0.0319 in |
UL 746 |
| 65.0 °C @Thickness 1.50 mm |
149 °F @Thickness 0.0590 in |
UL 746 | |
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
UL 746 | |
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.810 mm |
149 °F @Thickness 0.0319 in |
UL 746 |
| 65.0 °C @Thickness 1.50 mm |
149 °F @Thickness 0.0590 in |
UL 746 | |
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
UL 746 | |
| Flammability, UL94 | HB @Thickness 0.810 mm |
HB @Thickness 0.0319 in |
|
| Oxygen Index | 24 % | 24 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 11.8 kV/mm @Thickness 3.00 mm |
300 kV/in @Thickness 0.118 in |
ASTM D149 |
| Comparative Tracking Index | 500 V | 500 V | UL 746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 218 - 235 °C | 425 - 455 °F | |
| Middle Barrel Temperature | 246 - 257 °C | 475 - 495 °F | |
| Front Barrel Temperature | 246 - 268 °C | 475 - 515 °F | |
| Nozzle Temperature | 246 - 268 °C | 475 - 515 °F | |
| Melt Temperature | 249 - 266 °C | 480 - 510 °F | Processing Temperature |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Suggested Regrind, max | 25 |