Teknor Apex Chemlon® 100 W Nylon 66, Unreinforced

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant
Manufacturer Teknor Apex Company
Trade Name Chemlon®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Teknor Apex Chemlon® 100 W Nylon 66, Unreinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Notes: MoS2 modified; Molybdenum disulphide modified to provide self-lubrication and low friction to parts subjected to wear and abrasion. FMVSS Flammability: Passes, FMVSS 302Processing Method: Injection Molding Forms: PelletsInformation Provided by Teknor Apex
Physical Properties Metric English Comments
Specific Gravity 1.16 g/cc
1.16 g/cc
ASTM D792
Linear Mold Shrinkage 0.012 - 0.018 cm/cm
0.012 - 0.018 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength 93.1 MPa
13500 psi
ASTM D638
Elongation at Break 7.0 %
7.0 %
ASTM D638
Elongation at Yield 4.5 %
4.5 %
ASTM D638
Flexural Strength 117 MPa
17000 psi
ASTM D790
Flexural Modulus 3.10 GPa
450 ksi
ASTM D790
Izod Impact, Notched 0.641 J/cm

@Temperature 22.8 °C
1.20 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Thermal Properties Metric English Comments
Melting Point 257 °C
495 °F
DSC
Deflection Temperature at 1.8 MPa (264 psi) 107 °C
225 °F
Unannealed; ASTM D648
Flammability, UL94 V-2

@Thickness 0.749 mm
V-2

@Thickness 0.0295 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+18 ohm-cm
1.00e+18 ohm-cm
ASTM D257
Dielectric Strength 16.9 kV/mm

@Thickness 3.00 mm
430 kV/in

@Thickness 0.118 in
ASTM D149
Processing Properties Metric English Comments
Rear Barrel Temperature 241 - 254 °C
465 - 490 °F
Middle Barrel Temperature 257 - 271 °C
495 - 520 °F
Front Barrel Temperature 263 - 279 °C
505 - 535 °F
Melt Temperature 263 - 282 °C
505 - 540 °F
Processing Temperature
Drying Temperature 79.4 °C
175 °F