Teknor Apex Chemlon® 100 Nylon 66, Unreinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant |
| Manufacturer | Teknor Apex Company |
| Trade Name | Chemlon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teknor Apex Chemlon® 100 Nylon 66, Unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Basic nylon 66 with internal lubrication. Widely used for automotive, electronic and appliance applications. Processing Method: Injection Molding Forms: Pellets Automotive Specifications: Ford ESB-M4D150-A; Ford ESF-M4D150-AInformation Provided by Teknor Apex
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Water Absorption | 1.2 % | 1.2 % | 24 hr; ASTM D750 |
| Linear Mold Shrinkage | 0.015 - 0.022 cm/cm | 0.015 - 0.022 in/in | ASTM D955 |
| Melt Flow | 10.0 g/10 min @Load 0.325 kg, Temperature 235 °C |
10.0 g/10 min @Load 0.716 lb, Temperature 455 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 86.2 MPa | 12500 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 2.86 GPa | 415 ksi | ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm @Temperature 22.8 °C |
1.10 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.2 µm/m-°C | 39.0 µin/in-°F | ASTM D696 |
| Melting Point | 257 °C | 495 °F | DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.6 °C | 195 °F | Unannealed; ASTM D648 |
| UL RTI, Electrical | 115 °C @Thickness 0.810 mm |
239 °F @Thickness 0.0319 in |
UL 746 |
| 115 °C @Thickness 1.50 mm |
239 °F @Thickness 0.0590 in |
UL 746 | |
| 115 °C @Thickness 3.00 mm |
239 °F @Thickness 0.118 in |
UL 746 | |
| UL RTI, Mechanical with Impact | 75.0 °C @Thickness 0.810 mm |
167 °F @Thickness 0.0319 in |
UL 746 |
| 75.0 °C @Thickness 1.50 mm |
167 °F @Thickness 0.0590 in |
UL 746 | |
| 85.0 °C @Thickness 3.00 mm |
185 °F @Thickness 0.118 in |
UL 746 | |
| UL RTI, Mechanical without Impact | 95.0 °C @Thickness 0.810 mm |
203 °F @Thickness 0.0319 in |
UL 746 |
| 95.0 °C @Thickness 1.50 mm |
203 °F @Thickness 0.0590 in |
UL 746 | |
| 95.0 °C @Thickness 3.00 mm |
203 °F @Thickness 0.118 in |
UL 746 | |
| Flammability, UL94 | V-2 | V-2 | |
| Oxygen Index | 27 % | 27 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+18 ohm-cm | 1.00e+18 ohm-cm | ASTM D257 |
| Dielectric Strength | 18.1 kV/mm @Thickness 3.00 mm |
460 kV/in @Thickness 0.118 in |
ASTM D149 |
| Comparative Tracking Index | 600 V | 600 V | UL 746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 241 - 254 °C | 465 - 490 °F | |
| Middle Barrel Temperature | 257 - 274 °C | 495 - 525 °F | |
| Front Barrel Temperature | 263 - 282 °C | 505 - 540 °F | |
| Nozzle Temperature | 263 - 279 °C | 505 - 535 °F | |
| Melt Temperature | 263 - 279 °C | 505 - 535 °F | Processing Temperature |
| Drying Temperature | 79.4 °C | 175 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Suggested Moisture, max | 0.2 | |
| Suggested Regrind, max | 25 |