- Teknor Apex Beetle® 102 Nylon 66, Unreinforced, Nucleated
Teknor Apex Beetle® 102 Nylon 66, Unreinforced, Nucleated
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Nucleated , Nylon 66, Unreinforced, Flame Retardant |
| Manufacturer | Teknor Apex Company |
| Trade Name | Beetle® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teknor Apex Beetle® 102 Nylon 66, Unreinforced, Nucleated.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Notes: Nucleated for fast cycling; Improved strength and rigidity; FMVSS Flammability: Passes, FMVSS 302Processing Method: Injection Molding Forms: PelletsInformation Provided by Teknor Apex
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Water Absorption | 1.3 % | 1.3 % | 24 hr; ASTM D750 |
| Linear Mold Shrinkage | 0.010 - 0.016 cm/cm | 0.010 - 0.016 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 89.6 MPa | 13000 psi | ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | ASTM D638 |
| Elongation at Yield | 4.5 % | 4.5 % | ASTM D638 |
| Flexural Strength | 117 MPa | 17000 psi | ASTM D790 |
| Flexural Modulus | 3.10 GPa | 450 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm @Temperature 22.8 °C |
1.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.2 µm/m-°C | 39.0 µin/in-°F | ASTM D696 |
| Melting Point | 257 °C | 495 °F | DSC |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.6 °C | 195 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+18 ohm-cm | 1.00e+18 ohm-cm | ASTM D257 |
| Dielectric Strength | 16.9 kV/mm @Thickness 3.00 mm |
430 kV/in @Thickness 0.118 in |
ASTM D149 |
| Comparative Tracking Index | 600 V | 600 V | UL 746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 241 - 254 °C | 465 - 490 °F | |
| Middle Barrel Temperature | 257 - 271 °C | 495 - 520 °F | |
| Front Barrel Temperature | 263 - 279 °C | 505 - 535 °F | |
| Nozzle Temperature | 263 - 282 °C | 505 - 540 °F | |
| Melt Temperature | 263 - 282 °C | 505 - 540 °F | Processing Temperature |
| Drying Temperature | 79.4 °C | 175 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Suggested Moisture, max | 0.2 | |
| Suggested Regrind, max | 25 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P2620 TPE, PP Overmold or Standalone use
- ExxonMobil Santoprene® 121-65M300 Thermoplastic Elastomer (discontinued **)
- Mallard Creek Polymers Tykote® 1005 Styrene-Butadiene Emulsion
- Kolon KOPA® KN133G15 G/F Reinforced Nylon 6
- Eurotec® Tecodur® PB70 GR15 NL TD 28 PBT 15% glass fiber reinforced, UL94 V0, impact modified, high CTI
- CEN® Electronic Material CN Polyimide Film, 3 Mil Thickness
- Alliance N-42H Neodymium Iron Boron Magnetic Material
- DuPont Performance Polymers VTR 8525 (GBLT-S) GLT 505 Formulation (discontinued **)
Copyright © lookpolymers.com All Rights Reserved