- Teijin Panlite® LV-2225Y Standard (mold release/ice color grade) Polycarbonate Resin
Teijin Panlite® LV-2225Y Standard (mold release/ice color grade) Polycarbonate Resin
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Teijin |
| Trade Name | Panlite® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teijin Panlite® LV-2225Y Standard (mold release/ice color grade) Polycarbonate Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant and mold release grade, while maintaining intrinsic transparency of polycarbonate resin. It is suitable for injection molding applications, required to be slightly high fluidity.Applications:Electric, electronic and business machine components that need flame retardance and transparencySlightly thin wall or large moldingsInformation provided by Teijin Chemicals Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Water Absorption | 0.20 % | 0.20 % | in water, 23°C, 24h; ISO 62 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm @Thickness 4.00 mm |
0.0050 - 0.0070 in/in @Thickness 0.157 in |
|
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 4.00 mm |
0.0050 - 0.0070 in/in @Thickness 0.157 in |
|
| Melt Flow | 13.2 g/10 min @Load 1.20 kg, Temperature 300 °C |
13.2 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 61.0 MPa | 8850 psi | 50mm/min; ISO 527 |
| Elongation at Break | >= 50 % | >= 50 % | 50mm/min; ISO 527 |
| Elongation at Yield | 6.0 % | 6.0 % | 50mm/min; ISO 527 |
| Tensile Modulus | 2.40 GPa | 348 ksi | 1mm/min; ISO 527 |
| Flexural Strength | 92.0 MPa | 13300 psi | 2mm/min; ISO 178 |
| Flexural Modulus | 2.35 GPa | 341 ksi | 2mm/min; ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 7.10 J/cm² | 33.8 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 µm/m-°C @Temperature 20.0 °C |
38.9 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature 20.0 °C |
38.9 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | ISO 75 |
| Vicat Softening Point | 148 °C | 298 °F | 50°C/hr, 50N; ISO 306 |
| UL RTI, Electrical | 125 °C @Thickness 1.47 mm |
257 °F @Thickness 0.0579 in |
UL 746B |
| UL RTI, Mechanical with Impact | 115 °C @Thickness 1.47 mm |
239 °F @Thickness 0.0579 in |
UL 746B |
| UL RTI, Mechanical without Impact | 125 °C @Thickness 1.47 mm |
257 °F @Thickness 0.0579 in |
UL 746B |
| Flammability, UL94 | V-2 @Thickness 0.380 mm |
V-2 @Thickness 0.0150 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.585 | 1.585 | ASTM D542 |
| Transmission, Visible | 88 % @Thickness 3.00 mm |
88 % @Thickness 0.118 in |
ASTM D1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.0 @Frequency 1e+6 Hz |
3.0 @Frequency 1e+6 Hz |
IEC 60250 |
| 3.1 @Frequency 100 Hz |
3.1 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243 |
| Dissipation Factor | 0.0010 @Frequency 100 Hz |
0.0010 @Frequency 100 Hz |
IEC 60250 |
| 0.0090 @Frequency 1e+6 Hz |
0.0090 @Frequency 1e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 250 V | 250 V | IEC 60112 |