Teijin Panlite® LN-3000RM High Light Reflection, Halogen-Free Flame Resistant Polycarbonate Resin

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded
Manufacturer Teijin
Trade Name Panlite®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Teijin Panlite® LN-3000RM High Light Reflection, Halogen-Free Flame Resistant Polycarbonate Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polycarbonate-resin-based halogen-free flame retardant and good light-reflection grade. It exhibits high light-reflection (over 96 %) at whole visible light range and also good light shut-out even at a thinner thickness portion.Applications:Electric and electronic components that need high light reflection and light shut-out.Information provided by Teijin Chemicals Ltd.
Physical Properties Metric English Comments
Density 1.29 g/cc
0.0466 lb/in³
ISO 1183
Water Absorption 0.20 %
0.20 %
in water, 23°C, 24h; ISO 62
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm

@Thickness 4.00 mm
0.0040 - 0.0060 in/in

@Thickness 0.157 in
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm

@Thickness 4.00 mm
0.0040 - 0.0060 in/in

@Thickness 0.157 in
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
50mm/min; ISO 527
Tensile Strength, Yield 55.0 MPa
7980 psi
50mm/min; ISO 527
Elongation at Break 110 %
110 %
50mm/min; ISO 527
Elongation at Yield 6.0 %
6.0 %
50mm/min; ISO 527
Tensile Modulus 3.00 GPa
435 ksi
1mm/min; ISO 527
Flexural Strength 93.0 MPa
13500 psi
2mm/min; ISO 178
Flexural Modulus 2.70 GPa
392 ksi
2mm/min; ISO 178
Charpy Impact Unnotched NB
NB
ISO 179
Charpy Impact, Notched 6.00 J/cm²
28.6 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
CTE, linear 70.0 µm/m-°C

@Temperature 20.0 °C
38.9 µin/in-°F

@Temperature 68.0 °F
ISO 11359
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature 20.0 °C
38.9 µin/in-°F

@Temperature 68.0 °F
ISO 11359
Deflection Temperature at 0.46 MPa (66 psi) 98.0 °C
208 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 92.0 °C
198 °F
ISO 75
Vicat Softening Point 100 °C
212 °F
50°C/hr, 50N; ISO 306
UL RTI, Electrical 80.0 °C

@Thickness 1.47 mm
176 °F

@Thickness 0.0579 in
UL 746B
UL RTI, Mechanical with Impact 80.0 °C

@Thickness 1.47 mm
176 °F

@Thickness 0.0579 in
UL 746B
UL RTI, Mechanical without Impact 80.0 °C

@Thickness 1.47 mm
176 °F

@Thickness 0.0579 in
UL 746B
Flammability, UL94 V-2

@Thickness 0.400 mm
V-2

@Thickness 0.0157 in
V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.4

@Frequency 100 Hz
3.4

@Frequency 100 Hz
IEC 60250
3.4

@Frequency 1e+6 Hz
3.4

@Frequency 1e+6 Hz
IEC 60250
Dielectric Strength 32.0 kV/mm
813 kV/in
IEC 60243
Dissipation Factor 0.0055

@Frequency 100 Hz
0.0055

@Frequency 100 Hz
IEC 60250
0.010

@Frequency 1e+6 Hz
0.010

@Frequency 1e+6 Hz
IEC 60250
Comparative Tracking Index 250 V
250 V
IEC 60112