- Teijin Panlite® B-8130R Carbon Fiber Reinforced Polycarbonate Resin
Teijin Panlite® B-8130R Carbon Fiber Reinforced Polycarbonate Resin
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Carbon Fiber Reinforced |
| Manufacturer | Teijin |
| Trade Name | Panlite® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teijin Panlite® B-8130R Carbon Fiber Reinforced Polycarbonate Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
CF 30% reinforced grade, meeting UL 94 V-2. It has excellent strength, stiffness, heat resistance and electric conductivity. Other features are low molding shrinkage and dimensional accuracy.Applications:Mechanical, electric and electronic components that need stiffness and strengthMechanical, electric and electronic components that need extremely high dimensional accuracy.Mechanical, electric and electronic components that need electric conductivity or antistatic propertyInformation provided by Teijin Chemicals Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Water Absorption | 0.12 % | 0.12 % | in water, 23°C, 24h; ISO 62 |
| Linear Mold Shrinkage | 0.00010 - 0.0015 cm/cm @Thickness 4.00 mm |
0.00010 - 0.0015 in/in @Thickness 0.157 in |
|
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Thickness 4.00 mm |
0.0030 - 0.0050 in/in @Thickness 0.157 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 135 MPa | 19600 psi | 50mm/min; ISO 527 |
| Elongation at Break | 1.0 % | 1.0 % | 50mm/min; ISO 527 |
| Tensile Modulus | 18.1 GPa | 2630 ksi | 1mm/min; ISO 527 |
| Flexural Strength | 195 MPa | 28300 psi | 2mm/min; ISO 178 |
| Flexural Modulus | 16.0 GPa | 2320 ksi | 2mm/min; ISO 178 |
| Charpy Impact Unnotched | 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 10.0 µm/m-°C @Temperature 20.0 °C |
5.56 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature 20.0 °C |
27.8 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 149 °C | 300 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 147 °C | 297 °F | ISO 75 |
| Vicat Softening Point | 153 °C | 307 °F | 50°C/hr, 50N; ISO 306 |
| UL RTI, Electrical | 80.0 °C @Thickness 1.47 mm |
176 °F @Thickness 0.0579 in |
UL 746B |
| UL RTI, Mechanical with Impact | 80.0 °C @Thickness 1.47 mm |
176 °F @Thickness 0.0579 in |
UL 746B |
| UL RTI, Mechanical without Impact | 80.0 °C @Thickness 1.47 mm |
176 °F @Thickness 0.0579 in |
UL 746B |
| Flammability, UL94 | V-2 @Thickness 0.750 mm |
V-2 @Thickness 0.0295 in |
|
| V-1 @Thickness 3.00 mm |
V-1 @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 0.010 - 1.0 ohm-cm | 0.010 - 1.0 ohm-cm | IEC 60093 |
| Surface Resistance | 1.0 - 10 ohm | 1.0 - 10 ohm | IEC 60093 |
Users viewing this material also viewed the following:
- Polimeros Mexicanos Rotolene® Natural Linear Medium Density Polyethylene
- Quadrant EPP TIVAR® 1000 PE-UHMW, virgin (ISO Data)
- Resinlab® CYNERGY CA6012 Adhesive
- Industrial Laminates/Norplex NP842 Paper Base Laminate (discontinued **)
- Spartech 3030-10005 PVC and Alloy Products for Wire and Cable
- Teknor Apex Telcar® TL-2545A Thermoplastic Elastomer
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane, 300ºF Cure Temperature
- Akzo Nobel Expancel® 551 DE 40 d42 Dry expanded microspheres
- Solvay Specialty Polymers Amodel® AS-1933 HS Polyphthalamide (PPA) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved