Techmer ES Luriblend® PA6/6 GF30 TL15 UV 30% Glass Filled

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled , Nylon 66, Heat Stabilized , Nylon 66, PTFE Filled
Manufacturer Techmer ES
Trade Name Luriblend®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Techmer ES Luriblend® PA6/6 GF30 TL15 UV 30% Glass Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightAdditive: Heat Stabilizer, UV Stabilizer and PTFE Lubricant(15%)Features: Lubricated, Good Wear Resistance, Low Friction, Good UV Resistance and Heat StabilizedAppearance: Natural ColorInformation provided by TP Composites, Inc.
Physical Properties Metric English Comments
Density 1.49 g/cc
0.0538 lb/in³
ASTM D792
Water Absorption 0.50 %

@Time 86400 sec
0.50 %

@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.0050 cm/cm

@Thickness 3.17 mm
0.0050 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 90
90
ASTM D785
Tensile Strength, Yield 149 MPa
21600 psi
ASTM D638
Elongation at Break 2.0 %
2.0 %
ASTM D638
Flexural Strength 224 MPa
32500 psi
ASTM D790
Flexural Modulus 8.96 GPa
1300 ksi
ASTM D790
Izod Impact, Notched 0.747 J/cm

@Thickness 3.17 mm
1.40 ft-lb/in

@Thickness 0.125 in
ASTM D256
Coefficient of Friction, Dynamic 0.28
0.28
ASTM D1894
Coefficient of Friction, Static 0.22
0.22
ASTM D1894
K (wear) Factor 36.3 x 10-8 mm³/N-M
18.0 x 10-10 in³-min/ft-lb-hr
Limiting Pressure Velocity 0.613 MPa-m/sec
17500 psi-ft/min
10 fpm
0.613 MPa-m/sec
17500 psi-ft/min
1000 fpm
0.701 MPa-m/sec
20000 psi-ft/min
100 fpm
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 27.0 µm/m-°C
15.0 µin/in-°F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 259 °C
498 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 254 °C
490 °F
Unannealed; ASTM D648
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
ASTM D257
Dielectric Strength 19.7 kV/mm
500 kV/in
Method A (Short-Time); ASTM D149