Techmer ES HiFillÂ® PP CO GF20 CC 20% Glass Filled

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer , Polypropylene with 20% Glass Fiber Filler
Manufacturer	Techmer ES
Trade Name	HiFill®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Techmer ES HiFillÂ® PP CO GF20 CC 20% Glass Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by WeightFeatures: Copolymer and Chemically CoupledInformation provided by TP Composites, Inc.

Physical Properties	Metric	English	Comments
Density	1.04 g/cc	0.0376 lb/inÂ³	ASTM D792
Water Absorption	0.050 % @Time 86400 sec	0.050 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.0050 cm/cm @Thickness 3.17 mm	0.0050 in/in @Thickness 0.125 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	100	100	ASTM D785
Tensile Strength, Yield	64.8 MPa	9400 psi	ASTM D638
Elongation at Break	4.0 %	4.0 %	ASTM D638
Flexural Strength	107 MPa	15500 psi	ASTM D790
Flexural Modulus	4.48 GPa	650 ksi	ASTM D790
Izod Impact, Notched	0.534 J/cm @Thickness 3.17 mm, Temperature -28.9 Â°C	1.00 ft-lb/in @Thickness 0.125 in, Temperature -20.0 Â°F	ASTM D256
	2.46 J/cm @Thickness 3.17 mm, Temperature 22.8 Â°C	4.60 ft-lb/in @Thickness 0.125 in, Temperature 73.0 Â°F	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	37.8 Âµm/m-Â°C	21.0 Âµin/in-Â°F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	149 Â°C	300 Â°F	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	127 Â°C	260 Â°F	Unannealed; ASTM D648
Flammability, UL94	HB	HB