Techmer ES HiFill® LDPE 0098 S LE
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LDPE |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® LDPE 0098 S LE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Unspecified Filler/ReinforAdditive: Heat StabilizerFeatures: Low ExtractablesInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.980 g/cc | 0.0354 lb/in³ | ASTM D792 |
| Water Absorption | 0.050 % @Time 86400 sec |
0.050 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.019 cm/cm @Thickness 3.17 mm |
0.019 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 10.3 MPa | 1500 psi | ASTM D638 |
| Elongation at Break | 80 % | 80 % | ASTM D638 |
| Flexural Strength | 15.2 MPa | 2200 psi | ASTM D790 |
| Flexural Modulus | 0.276 GPa | 40.0 ksi | ASTM D790 |
| Izod Impact, Notched | 2.67 J/cm @Thickness 3.17 mm |
5.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 34.2 µm/m-°C | 19.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.8 °C | 190 °F | Unannealed; ASTM D648 |
Users viewing this material also viewed the following: