Techmer ES Elastoblend® TPX-PA6/6 97058 BK 32% Mineral Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Mineral Filled , Nylon 66, Mineral Filled, Impact Grade |
| Manufacturer | Techmer ES |
| Trade Name | Elastoblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Elastoblend® TPX-PA6/6 97058 BK 32% Mineral Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Mineral Fiber Reinforcement, 33% Filler by WeightAdditive: Impact Modifier and LubricantFeatures: Impact Modified and LubricatedUL File Number: E157318Appearance: BlackProcessing Method: Injection MoldingInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 |
| Water Absorption | 0.70 % @Time 86400 sec |
0.70 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm @Thickness 3.17 mm |
0.010 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength | 77.2 MPa | 11200 psi | ASTM D638 |
| Elongation at Yield | 16 % | 16 % | ASTM D638 |
| Flexural Yield Strength | 116 MPa | 16800 psi | ASTM D790 |
| Flexural Modulus | 4.52 GPa | 655 ksi | ASTM D790 |
| Izod Impact, Notched | 1.01 J/cm @Thickness 3.17 mm |
1.90 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 14.9 J/cm @Thickness 3.17 mm |
28.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 54.0 µm/m-°C | 30.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 420 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+13 ohm-cm | 2.00e+13 ohm-cm | ASTM D257 |
| Dielectric Strength | 15.0 kV/mm | 380 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Polimeri Europa Eraclene® FA 706 Hexene Copolymer High Density Polyethylene - Blown Film Extrusion
- SABIC Innovative Plastics Cycoloy® CY201 PC+ABS (Europe-Africa-Middle East)
- PolyOne Geon™ 210 Series 217 Blending Resin Polyvinyl Chloride Homopolymer (PVC Homopolymer)
- Permabond 931 Cyanoacrylate
- Isoflon PTFE + 60% Bronze Polytetrafluoroethylene with 60% Bronze
- Styrolution PS 158 N/L GPPS
- SABIC Innovative Plastics NORYL GTX GTX810 PPE+PA (Europe-Africa-Middle East)
- DuPont Performance Polymers VESPEL TP-8792 Polyimide
- ConocoPhillips Hydroclear® 46 Multipurpose R&O Oil, AGMA Lubricant No. 1
- Beijing Evergrow Resources UHMW PE Bar
Copyright © lookpolymers.com All Rights Reserved