Techmer ES Elastoblend® PA6/66 IM 6040 MB
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, Unreinforced |
| Manufacturer | Techmer ES |
| Trade Name | Elastoblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Elastoblend® PA6/66 IM 6040 MB.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsAdditive: Nucleating Agent, Heat Stabilizer, Lubricant and Impact ModifierFeatures: Copolymer, Nucleated, Heat Stabilized, Lubricant and Impact ModifiedInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | ASTM D792 |
| Water Absorption | 1.5 % @Time 86400 sec |
1.5 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm @Thickness 3.17 mm |
0.013 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Yield | 55.8 MPa | 8100 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Flexural Strength | 83.4 MPa | 12100 psi | ASTM D790 |
| Flexural Modulus | 1.86 GPa | 270 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
2.00 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| 2.14 J/cm @Thickness 3.17 mm, Temperature -20.0 °C |
4.00 ft-lb/in @Thickness 0.125 in, Temperature -4.00 °F |
ASTM D256 | |
| 3.74 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
7.00 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 95.4 µm/m-°C | 53.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 174 °C | 345 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 18.1 kV/mm | 460 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 45 PHR N330 Filler
- Idemitsu Kosan Xarec® WA 212 SPS, 30% Glass Filled
- LG Chemical SEETEC R3400 Polypropylene Random Copolymer
- Sibur DST-30R-01 2nd Group Styrene-Butadiene-Styrene Block Copolymer (SBS-TPE)
- SABIC Innovative Plastics Ultem 1010KM PEI
- Saint-Gobain Tygothane® C-544-AI.B. Precision Polyurethane Pressure Tubing Formulation
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 76A
- DAK Americas Laser+® C K62A PET
- Fainplast Compounds GS 7816 Flexible PVC, Injection Molding for Footwear
- Aclo Accutech Polypropylene Homopolymer HP0339T40L Talc Reinforced
Copyright © lookpolymers.com All Rights Reserved