TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 25A, Non-Black Sulfur Cure

Category Polymer , Thermoset , Polyester, TS , Polyurethane, TS , Thermoset Polyurethane, Elastomer, Unreinforced , Rubber or Thermoset Elastomer (TSE)
Manufacturer TSE Industries, Inc
Trade Name Millathane®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 25A, Non-Black Sulfur Cure.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Millathane® 76 is a very suitable choice for use in products such as bushings, small copier rolls; automotive applications — bumpers, o-rings, hydraulic seals, belts, gaskets, solid tires — and many other high performance polyurethane applications. Millathane 76 can be vulcanized by sulfur or peroxide cured systems.Many applications exist for Millathane®76 compounds in a low durometer range from 25A to 40A. These include — printing rolls, copier rolls, can tester pads, spinner rings, belting, suction cups, vibration damping bumpers, and other specialized applications. The reason it's chosen for these low hardness applications — its excellent cut and tear strength, abrasion resistance, and overall toughness.FormulationMillathane 76 100.0AC Poly 617A2.0Akrofax 11LG2.5Cumar P-105.0TP-9528.0Stantone Green0.3Zinc Stearate0.5MBTS4.0MBT2.0Thanecure® ZM1.0Sulfur1.5All information provided by TSE Industries
Mechanical Properties Metric English Comments
Hardness, Shore A 25
25
Tensile Strength, Yield 13.14 MPa
1906 psi
Elongation at Yield 578 %
578 %
100% Modulus 0.000524 GPa
0.0760 ksi
200% Modulus 0.000841 GPa
0.122 ksi
300% Modulus 0.00125 GPa
0.182 ksi
Tear Strength 16.5 kN/m
94.1 pli
Die C
Processing Properties Metric English Comments
Cure Time 15.0 min

@Temperature 149 °C
0.250 hour

@Temperature 300 °F