TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 60 PHR N330 (HAF) Black

Category Polymer , Thermoset , Polyester, TS , Polyurethane, TS , Thermoset Polyurethane, Elastomer, Unreinforced , Rubber or Thermoset Elastomer (TSE)
Manufacturer TSE Industries, Inc
Trade Name Millathane®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 60 PHR N330 (HAF) Black.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is carried out by the use of various peroxides including dicumyl peroxide (DCP) or 2,5-dimethyl-2,5-bis (t-butylperoxy) hexane (DBPH).FormulationMillathane 5004100Stearic Acid0.25N330 (HAF) Black60Di-Cup 40C5.3All information provided by TSE Industries
Mechanical Properties Metric English Comments
Hardness, Shore A 84
84
heat aged one week at 300ºF
86
86
89
89
heat aged 70 hours at 300ºF
Tensile Strength, Yield 10.3 MPa
1500 psi
heat aged one week at 300ºF
14.5 MPa
2100 psi
heat aged 70 hours at 300ºF
24.9 MPa
3610 psi
Elongation at Yield 220 %
220 %
heat aged 70 hours at 300ºF
230 %
230 %
heat aged one week at 300ºF
280 %
280 %
100% Modulus 0.00483 GPa
0.700 ksi
heat aged one week at 300ºF
0.00655 GPa
0.950 ksi
heat aged 70 hours at 300ºF
0.00993 GPa
1.44 ksi
200% Modulus 0.00793 GPa
1.15 ksi
heat aged one week at 300ºF
0.0131 GPa
1.90 ksi
heat aged 70 hours at 300ºF
0.0207 GPa
3.00 ksi
Processing Properties Metric English Comments
Cure Time 30.0 min

@Temperature 152 °C
0.500 hour

@Temperature 305 °F