TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 20 PHR N330 (HAF) Black

Category Polymer , Thermoset , Polyester, TS , Polyurethane, TS , Thermoset Polyurethane, Elastomer, Unreinforced , Rubber or Thermoset Elastomer (TSE)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 20 PHR N330 (HAF) Black.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is carried out by the use of various peroxides including dicumyl peroxide (DCP) or 2,5-dimethyl-2,5-bis (t-butylperoxy) hexane (DBPH).FormulationMillathane 5004100Stearic Acid0.25N330 (HAF) Black20Di-Cup 40C4.0All information provided by TSE Industries
Mechanical Properties Metric English Comments
Hardness, Shore A 57
57
heat aged one week at 300ºF
64
64
heat aged 70 hours at 300ºF
68
68
Tensile Strength, Yield 11.1 MPa
1610 psi
heat aged one week at 300ºF
20.3 MPa
2950 psi
heat aged 70 hours at 300ºF
31.7 MPa
4600 psi
Elongation at Yield 440 %
440 %
heat aged one week at 300ºF
460 %
460 %
460 %
460 %
heat aged 70 hours at 300ºF
100% Modulus 0.00145 GPa
0.210 ksi
heat aged one week at 300ºF
0.00241 GPa
0.350 ksi
heat aged 70 hours at 300ºF
0.00414 GPa
0.600 ksi
200% Modulus 0.00400 GPa
0.580 ksi
heat aged one week at 300ºF
0.00655 GPa
0.950 ksi
heat aged 70 hours at 300ºF
0.0103 GPa
1.50 ksi
300% Modulus 0.00696 GPa
1.01 ksi
heat aged one week at 300ºF
0.0126 GPa
1.83 ksi
heat aged 70 hours at 300ºF
0.0193 GPa
2.80 ksi
Processing Properties Metric English Comments
Cure Time 30.0 min

@Temperature 152 °C
0.500 hour

@Temperature 305 °F