TPI Porene® ABS-KU650 Super High Heat ABS Resin

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
Manufacturer Thai Petrochemical Industry Co. LTD.
Trade Name Porene®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF TPI Porene® ABS-KU650 Super High Heat ABS Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by US distributor Polymer Technology and Services, LLC (PTS).
Physical Properties Metric English Comments
Melt Flow 1.8 g/10 min

@Load 10.0 kg,
Temperature 220 °C
1.8 g/10 min

@Load 22.0 lb,
Temperature 428 °F
Mechanical Properties Metric English Comments
Hardness, Rockwell R 110
110
ASTM D785
Tensile Strength, Yield 44.0 MPa

@Thickness 3.17 mm
6380 psi

@Thickness 0.125 in
Flexural Yield Strength 63.4 MPa

@Thickness 3.17 mm
9200 psi

@Thickness 0.125 in
Flexural Modulus 2.07 GPa

@Thickness 3.17 mm
300 ksi

@Thickness 0.125 in
Izod Impact, Notched 1.39 J/cm

@Thickness 3.17 mm
2.60 ft-lb/in

@Thickness 0.125 in
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 122 °C
252 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 113 °C
235 °F
ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 193 °C
380 °F
Middle Barrel Temperature 216 °C
420 °F
Front Barrel Temperature 232 °C
450 °F
Melt Temperature 246 - 260 °C
475 - 500 °F
Nozzle temp not greater than stock
Mold Temperature 48.9 - 65.6 °C
120 - 150 °F
Drying Temperature 87.8 - 93.3 °C
190 - 200 °F
Dry Time 2 - 24 hour
2 - 24 hour
Injection Pressure 68.9 - 82.7 MPa
10000 - 12000 psi
Back Pressure 0.689 MPa
100 psi
Screw Speed 50 - 60 rpm
50 - 60 rpm
Descriptive Properties Value Comments
Injection Fill Speed Slow to Moderate