TIMET TIMETAL® 6-4 ELI Titanium Alloy (Ti-6Al-4V ELI; ASTM Grade 23) (Annealed; 2.50 - 4.00 in Rod or Thickness; Per ASTM F136)

Category Metal , Nonferrous Metal , Titanium Alloy , Alpha/Beta Titanium Alloy
Manufacturer TIMET
Trade Name TIMETAL®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF TIMET TIMETAL® 6-4 ELI Titanium Alloy (Ti-6Al-4V ELI; ASTM Grade 23) (Annealed; 2.50 - 4.00 in Rod or Thickness; Per ASTM F136).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to this MatWeb entry; other specific form/thickness entries are also available in MatWeb.Features: A lower strength version of TIMETAL 6-4 with improved toughness, cryogenic ductility, and SCC resistance. Major uses are in the medical implant field, marine structural components, and oil and gas production. This variant is available for fracture critical applications. This alloy is available in most common product forms including billet, bar, wire, plate, and sheet. Data provided by TIMET.
Physical Properties Metric English Comments
Density 4.42 g/cc
0.160 lb/in³
Typical
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate >= 825 MPa
>= 120000 psi
L, LT and ST Directions
Tensile Strength, Yield >= 760 MPa

@Strain 0.200 %
>= 110000 psi

@Strain 0.200 %
L, LT and ST Directions
Elongation at Break >= 8.0 %
>= 8.0 %
L, LT and ST Directions
Reduction of Area >= 15 %
>= 15 %
0.2% YS; L, LT and ST Directions
Modulus of Elasticity 105 - 120 GPa
15200 - 17400 ksi
Typical
Poissons Ratio 0.31
0.31
Shear Modulus 41.0 - 45.0 GPa
5950 - 6530 ksi
Bend Radius, Minimum 5.0 t

@Thickness 2.00 mm
5.0 t

@Thickness 0.0787 in
Typical; sheet
Thermal Properties Metric English Comments
CTE, linear 9.00 µm/m-°C

@Temperature 0.000 - 100 °C
5.00 µin/in-°F

@Temperature 32.0 - 212 °F
9.40 µm/m-°C

@Temperature 20.0 - 425 °C
5.22 µin/in-°F

@Temperature 68.0 - 797 °F
9.70 µm/m-°C

@Temperature 20.0 - 650 °C
5.39 µin/in-°F

@Temperature 68.0 - 1200 °F
Specific Heat Capacity 0.586 J/g-°C
0.140 BTU/lb-°F
Melting Point 1674 °C
3045 °F
Liquidus >= 1636 °C
>= 2977 °F
Maximum Service Temperature, Air 350 °C
662 °F
Reasonable mechanical properties retained
Beta Transus 982 °C
1800 °F
Component Elements Properties Metric English Comments
Aluminum, Al 5.5 - 6.5 %
5.5 - 6.5 %
Carbon, C <= 0.080 %
<= 0.080 %
Hydrogen, H <= 0.0125 %
<= 0.0125 %
Iron, Fe <= 0.25 %
<= 0.25 %
Nitrogen, N <= 0.030 %
<= 0.030 %
Oxygen, O <= 0.13 %
<= 0.13 %
Titanium, Ti 88.1 - 91 %
88.1 - 91 %
Calculated as remainder
Vanadium, V 3.5 - 4.5 %
3.5 - 4.5 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.000168 ohm-cm
0.000168 ohm-cm
Magnetic Permeability 1.00005
1.00005
at 20 oersteds