TIMET TIMETAL® 6-2-4-6 Titanium Alloy (Ti-6Al-2Sn-4Zr-6Mo), 50% Equiaxed Alpha + STOA

Category Metal , Nonferrous Metal , Titanium Alloy , Alpha/Beta Titanium Alloy
Manufacturer TIMET
Trade Name TIMETAL®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF TIMET TIMETAL® 6-2-4-6 Titanium Alloy (Ti-6Al-2Sn-4Zr-6Mo), 50% Equiaxed Alpha + STOA.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This entry has UTS, TYS, Elongation, ROA, and fatigue values specific to material in the 50% Equiaxed Alpha + STOA (885°C/1hr/AC + 705°C/1hr/AC) condition. Other data below are typical of TIMETAL® 6-2-4-6. High-Strength, Intermediate Temperature AlloyFeatures: TIMETAL 6-2-4-6 is a stronger derivative of TIMETAL 6-2-4-2 offering higher strength, depth hardenability and elevated temperature properties up to 450°C. This alloy is similar in forgeability and crack sensitivity to TIMETAL 6-4. This alloy is used in intermediate compressor stages of turbine engines for disks and blades, seals, and for airframe parts. It is nonmagnetic.Data provided by TIMET.
Physical Properties Metric English Comments
Density 4.64 g/cc
0.168 lb/in³
Typical
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 1144 MPa
165900 psi
Tensile Strength, Yield 1068 MPa
154900 psi
Elongation at Break 14 %
14 %
Reduction of Area 41 %
41 %
Modulus of Elasticity 115 GPa
16700 ksi
Typical
Fatigue Strength 262 MPa

@# of Cycles 1.00e+7
38000 psi

@# of Cycles 1.00e+7
notched
620 MPa

@# of Cycles 1.00e+7
89900 psi

@# of Cycles 1.00e+7
smooth
Thermal Properties Metric English Comments
CTE, linear 9.00 µm/m-°C

@Temperature 20.0 - 100 °C
5.00 µin/in-°F

@Temperature 68.0 - 212 °F
Specific Heat Capacity 0.502 J/g-°C
0.120 BTU/lb-°F
Thermal Conductivity 7.61 W/m-K
52.8 BTU-in/hr-ft²-°F
Melting Point 1595 - 1675 °C
2903 - 3047 °F
Solidus 1595 °C
2903 °F
Liquidus 1675 °C
3047 °F
Beta Transus 940 °C
1720 °F
Component Elements Properties Metric English Comments
Aluminum, Al 5.5 - 6.5 %
5.5 - 6.5 %
Carbon, C <= 0.040 %
<= 0.040 %
Hydrogen, H <= 0.125 %
<= 0.125 %
Iron, Fe <= 0.15 %
<= 0.15 %
Molybdenum, Mo 5.5 - 6.5 %
5.5 - 6.5 %
Nitrogen, N <= 0.040 %
<= 0.040 %
Oxygen, O <= 0.15 %
<= 0.15 %
Tin, Sn 1.75 - 2.25 %
1.75 - 2.25 %
Titanium, Ti 79.4 - 83.7 %
79.4 - 83.7 %
Calculated as remainder
Zirconium, Zr 3.6 - 4.4 %
3.6 - 4.4 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.000190 - 0.000205 ohm-cm
0.000190 - 0.000205 ohm-cm