TIMET TIMETAL® 3-2.5 -0.05Pd Titanium Alloy

Category Metal , Nonferrous Metal , Titanium Alloy , Alpha/Near Alpha Titanium Alloy
Manufacturer TIMET
Trade Name TIMETAL®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF TIMET TIMETAL® 3-2.5 -0.05Pd Titanium Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Cold Workable Medium Strength Alloy. Palladium is added to this grade to enhance its corrosion behavior. Property data below is typical of TIMETAL® 3-2.5 Titanium Alloy.Data provided by TIMET.
Physical Properties Metric English Comments
Density 4.51 g/cc
0.163 lb/in³
Typical
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 650 MPa
94300 psi
Typical
Tensile Strength, Yield 550 MPa

@Strain 0.200 %
79800 psi

@Strain 0.200 %
Typical
Elongation at Break 15 %
15 %
Typical
Modulus of Elasticity 105 - 120 GPa
15200 - 17400 ksi
Typical
Poissons Ratio 0.30
0.30
Shear Modulus 43.0 - 45.0 GPa
6240 - 6530 ksi
Bend Radius, Minimum 2.5 t
2.5 t
Typical; on 0.078 in (2 mm) sheet
Thermal Properties Metric English Comments
CTE, linear 9.61 µm/m-°C

@Temperature 20.0 - 95.0 °C
5.34 µin/in-°F

@Temperature 68.0 - 203 °F
Thermal Conductivity 8.30 W/m-K

@Temperature 20.0 - 95.0 °C
57.6 BTU-in/hr-ft²-°F

@Temperature 68.0 - 203 °F
Melting Point <= 1700 °C
<= 3090 °F
Liquidus 1700 °C
3090 °F
Beta Transus 935 °C
1720 °F
Component Elements Properties Metric English Comments
Aluminum, Al 2.5 - 3.5 %
2.5 - 3.5 %
Carbon, C <= 0.080 %
<= 0.080 %
Hydrogen, H <= 0.015 %
<= 0.015 %
Iron, Fe <= 0.25 %
<= 0.25 %
Nitrogen, N <= 0.030 %
<= 0.030 %
Oxygen, O <= 0.15 %
<= 0.15 %
Palladium, Pd 0.040 - 0.080 %
0.040 - 0.080 %
Titanium, Ti 92.5 - 95.5 %
92.5 - 95.5 %
Calculated as remainder
Vanadium, V 2.0 - 3.0 %
2.0 - 3.0 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.000127 ohm-cm
0.000127 ohm-cm