TIMET CP Titanium (ASTM Grade 3)

Category Metal , Nonferrous Metal , Titanium Alloy , Unalloyed/Modified Titanium
Manufacturer TIMET
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF TIMET CP Titanium (ASTM Grade 3).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Commercially Pure Titanium. Industry Specifications: USA Aerospace: AMS 4900. Germany Aerospace: 3.7055. France: T-50. UK Aerospace Specification DTD 5023, 5273.Features: The mechanical properties of CP titanium are influenced by small additions of oxygen and iron. By careful control of these additions, the various grades of commercially pure titanium are produced to give properties suited to different applications. TIMETAL 65A is equivalent to ASTM Grade 3. It is a general purpose grade of commercially pure titanium that has excellent corrosion resistance in highly oxidizing to mildly reducing environments, including chlorides, and an excellent strength to weight ratio. It offers the highest ASME allowable design stresses of any commercially pure grade of titanium. 65A also has good impact properties at low temperatures. It can be satisfactorily welded, machined, cold worked, hot worked, and cast. It is nonmagnetic.Typical heat treatment for this alloy: Anneal at 700°C for 1 hour and air cool. Stress Relieve at 500°C for 30 mins and air cool. Data provided by TIMET.
Physical Properties Metric English Comments
Density 4.51 g/cc
0.163 lb/in³
Typical
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 585 MPa
84800 psi
Typical
Tensile Strength, Yield 450 MPa

@Strain 0.200 %
65300 psi

@Strain 0.200 %
Typical
Elongation at Break 25 %
25 %
Typical
Reduction of Area 48 %
48 %
Typical
Modulus of Elasticity 105 - 120 GPa
15200 - 17400 ksi
Typical
Fatigue Strength 116 MPa

@# of Cycles 1.00e+7
16800 psi

@# of Cycles 1.00e+7
Notched, Kt=4; rotating bend (sample with UTS = 589 MPa)
116 MPa

@# of Cycles 1.00e+7
16800 psi

@# of Cycles 1.00e+7
Notched, Kt=3.3; rotating bend (sample with UTS = 550 MPa)
123 MPa

@# of Cycles 1.00e+7
17800 psi

@# of Cycles 1.00e+7
Notched, Kt=3; rotating bend (sample with UTS = 589 MPa)
147 MPa

@# of Cycles 1.00e+7
21300 psi

@# of Cycles 1.00e+7
Notched, Kt=2; rotating bend (sample with UTS = 589 MPa)
170 MPa

@# of Cycles 1.00e+7
24700 psi

@# of Cycles 1.00e+7
Notched, Kt=2; rotating bend (sample with UTS = 550 MPa)
247 MPa

@# of Cycles 1.00e+7
35800 psi

@# of Cycles 1.00e+7
Notched, Kt=1.5; rotating bend (sample with UTS = 550 MPa)
263 MPa

@# of Cycles 1.00e+7
38100 psi

@# of Cycles 1.00e+7
Smooth, Kt=1; rotating bend (sample with UTS = 550 Mpa)
278 MPa

@# of Cycles 1.00e+7
40300 psi

@# of Cycles 1.00e+7
Smooth, Kt=1; rotating bend (sample with UTS = 589 Mpa)
Bend Radius, Minimum 2.5 t

@Thickness 2.00 mm
2.5 t

@Thickness 0.0787 in
Typical; sheet
Thermal Properties Metric English Comments
CTE, linear 8.60 µm/m-°C

@Temperature 20.0 - 100 °C
4.78 µin/in-°F

@Temperature 68.0 - 212 °F
9.50 µm/m-°C

@Temperature 20.0 - 300 °C
5.28 µin/in-°F

@Temperature 68.0 - 572 °F
9.70 µm/m-°C

@Temperature 20.0 - 500 °C
5.39 µin/in-°F

@Temperature 68.0 - 932 °F
Thermal Conductivity 21.79 W/m-K
151.2 BTU-in/hr-ft²-°F
Maximum Service Temperature, Air 425 °C
797 °F
Continuous
540 °C
1000 °F
Intermittent
Beta Transus 920 °C
1690 °F
Component Elements Properties Metric English Comments
Carbon, C <= 0.080 %
<= 0.080 %
Hydrogen, H <= 0.015 %
<= 0.015 %
Iron, Fe <= 0.30 %
<= 0.30 %
Nitrogen, N <= 0.050 %
<= 0.050 %
Oxygen, O <= 0.35 %
<= 0.35 %
Titanium, Ti >= 98.8 %
>= 98.8 %
As Remainder
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000540 ohm-cm
0.0000540 ohm-cm