TIMCAL TIMREX® F10 Primary Synthetic P/M Special-Graphite

Category Carbon , Graphite , Other Engineering Material , Additive/Filler for Polymer
Manufacturer TIMCAL
Trade Name TIMREX®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF TIMCAL TIMREX® F10 Primary Synthetic P/M Special-Graphite.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TIMREX Primary Synthetic Graphite is produced in a unique highly controlled graphitization process which assures narrow specifications and unequalled consistent quality due to: monitoring of all production and processing stages, strict final inspection, and clearly defined development processes.TIMREX Primary Synthetic Graphite shows unique properties thanks to the combination of a consistent purity, perfect crystalline structure and well defined texture.Applications: Fe-sintered engineering partsFe-self lubricating engineering partsFe-friction partscopper/bronze bearingsInformation provided by TIMCAL
Physical Properties Metric English Comments
Bulk Density 0.0900 g/cc
0.00325 lb/in³
Scott
7.10 g/cc
0.257 lb/in³
Sintered
Particle Size 6.8 µm
6.8 µm
d50
12.6 µm
12.6 µm
d90
Ash <= 0.60 %
<= 0.60 %
Mechanical Properties Metric English Comments
Hardness, Rockwell B 73

@Temperature 1135 °C,
Time 1800 sec
73

@Temperature 2075 °F,
Time 0.500 hour
at Target density of 6.6 g/cc
78

@Temperature 1135 °C,
Time 1800 sec
78

@Temperature 2075 °F,
Time 0.500 hour
at Target density of 6.8 g/cc
81

@Temperature 1135 °C,
Time 1800 sec
81

@Temperature 2075 °F,
Time 0.500 hour
at Target density of 67.0 g/cc
Rupture Strength 780 MPa

@Temperature 1120 °C,
Time 1500 sec
113000 psi

@Temperature 2050 °F,
Time 0.416 hour
at green density of 6.49 g/cc
990 MPa

@Temperature 1120 °C,
Time 1500 sec
144000 psi

@Temperature 2050 °F,
Time 0.416 hour
at green density of 6.87 g/cc
1070 MPa

@Temperature 1120 °C,
Time 1500 sec
155000 psi

@Temperature 2050 °F,
Time 0.416 hour
at green density of 7.02 g/cc
Descriptive Properties Value Comments
Crystallinity Height, Lc 80 nm