TIMCAL ENSACO™ 210G Conductive Carbon Black

Category Carbon , Carbon Black , Other Engineering Material , Additive/Filler for Polymer
Manufacturer TIMCAL
Trade Name ENSACO™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF TIMCAL ENSACO™ 210G Conductive Carbon Black.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ENSACO™ & SUPER P™ conductive carbon blacks are carbon blacks with a high to very high void volume allowing the retention of a carbon network at low to very low filler content. The void volume can originate from the interstices between the carbon black particle due to their complex arrangement and from the porosity.Applications:black pigmentUV stabilizerrubber reinforcementInformation provided by TIMCAL
Physical Properties Metric English Comments
Density 0.210 g/cc
0.00759 lb/in³
Pour Density; ASTM D1513
Volatiles <= 0.20 %
<= 0.20 %
Weight loss during heating between 105 and 950°C; Internal Method 02
Oil Absorption 155 %
155 %
OAN (Oil Absorption Number) ml/100g; ASTM D2414
Particle Size 45 µm
45 µm
2 ppm sieve residue; ASTM D1514
pH 8.0 - 11
8.0 - 11
ASTM D1512
Specific Surface Area 55 m²/g
55 m²/g
BET Nitrogen Surface Area; ASTM D3037
Mooney Viscosity 44
44
(1+4), EVA/NBR Strippable Compounds
Ash 0.10 %
0.10 %
ASTM D1506
Mechanical Properties Metric English Comments
Hardness, Shore A 90 - 94
90 - 94
EVA/NBR Strippable Compounds
Tensile Strength 1.90 - 16.9 MPa
276 - 2450 psi
EVA/NBR Strippable Compounds
Elongation at Break 130 - 180 %
130 - 180 %
EVA/NBR Strippable Compounds
100% Modulus 0.0122 GPa
1.77 ksi
EVA/NBR Strippable Compounds
Component Elements Properties Metric English Comments
Sulfur, S <= 0.50 %
<= 0.50 %
ASTM D1619
Electrical Properties Metric English Comments
Volume Resistivity <= 500 ohm-cm
<= 500 ohm-cm
25% carbon black in HDPE; Internal Method 11
6600 ohm-cm
6600 ohm-cm
EVA/NBR Strippable Compounds
Processing Properties Metric English Comments
Moisture Content 0.10 %
0.10 %
as packed; ASTM D1509
Descriptive Properties Value Comments
Aspect Fine black granules
COAN (Crushed OAN) ml/100g 95
ASTM D3493
Peel Strength 3 N
hot air 100°C, EVA/NBR Strippable Compounds
3 N
hot air 100°C after 21 days, EVA/NBR Strippable Compounds
4 N
hot air 100°C after 3 days, EVA/NBR Strippable Compounds
Toluene Extract, Max, % 0.1
ASTM D4527